Abstract:To explore the mechanical properties and fracture modes of basalt fiber-reinforced concrete, single-doped and hybrid-doped basalt fiber-reinforced concrete was prepared, and uniaxial failure tests under different basalt fiber-reinforced concrete contents were carried out. At the same time, the smooth kernel function in the traditional SPH method was improved, and the basalt fiber random generation algorithm was embedded in the SPH program to realize the simulation of the progressive failure of basalt fiber-reinforced concrete. The results show that under the circumstance with no basalt fiber, the specimen final failure mode is damage on the upper and lower surface, as well as the side edge, while the interior of the specimen center is basically intact, indicating that there is an obvious stress concentration phenomenon on the upper and lower surface when the specimen is compressed. Under the circumstance with basalt fiber, longitudinal cracks begin to appear inside the specimen. With the increase in the content, the crack location gradually develops from the edge to the middle, and the crack number gradually increases. This indicates that appropriately increasing the fiber content in concrete may improve the stress state of concrete, change the eccentric compression to axial compression, and indirectly increase the compressive strength of concrete. The numerical simulation results are consistent with the test results, verifying the rationality of the numerical simulation algorithm. For the concrete model without the basalt fiber, shear cracks are generated around the model. For the concrete model with basalt fiber, in addition to shear cracks, the tensile cracks generated at the basalt fiber inside the model eventually lead to the splitting failure of the model. The strength of concrete samples with basalt content of 0.1%, 0.2%, and 0.3% is increased by 1.69%, 5.10%, and 4.31%, respectively, compared to the concrete sample without basalt fiber. It can be seen that with the increase in the content of single-doped basalt fiber, the concrete strength is improved to a certain extent, but the improvement degree is not high; For hybrid-doped basalt fiber-reinforced concrete, the strength of concrete samples with basalt content of 0.1%, 0.2%, and 0.3% is increased by 14.51%, 15.02%, and 30.31%, respectively, compared to the concrete sample without basalt fiber. Therefore, compared with the single-doped basalt fiber process, hybrid doping is easier to improve the strength of concrete.

Fracture Behavior of Basalt Fiber‐reinforced Concrete Subjected to High Temperatures

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Experimental study on dynamic behavior of concrete at elevated temperatures

Correlation Between Macroscopic Properties and Microscopic Pore Structure in Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites Subjected to Elevated Temperatures

Influence of Basalt Fiber on the Mechanical Properties and Deformation Failure of Concrete after High Temperature

Research on Dynamic Mechanical Properties and Constitutive Model of Basalt Fiber Reinforced Concrete after Exposure to Elevated Temperatures under Impact Loading

Experimental Study on Basic Mechanical Properties of Basalt Fiber Reinforced Concrete

Experimental study on mechanical properties and breakage of high temperature carbon fiber-bar reinforced concrete under impact load

The Influence of Temperatures on the Mechanical Properties and Fracture Behavior of Rocks under Mixed Mode I/II Loading

Study on the Fracture Mechanical Properties of High Performance Concrete (HPC) with Rapid Cooling after High Temperature

Effects of High Temperature and Substitution Rates of Fly Ash on the Mechanical Properties and Microstructures of Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites

Experimental and Theoretical Study on Flexural Behavior of GFRP- and CFRP-Reinforced Concrete Beams after High-Temperature Exposure

Effect of Temperature Variation and Pre-Sustained Loading on the Bond Between Basalt FRP Sheets and Concrete.

Bonding Properties Between Steel-Basalt Hybrid Fibers Reinforced Cementitious Composites and Existing Concrete at High Temperatures

Effects of thermal treatment on the fracture behavior of rock-concrete bi-material specimens containing an interface crack

Experimental study on mechanical properties of basalt fiber reinforced nano-SiO2 concrete after high temperature

Experimental study on the triaxial compression mechanical performance of basalt fiber-reinforced recycled aggregate concrete after exposure to high temperature

Research on the fracture mechanical performance of basalt fiber nano-CaCO3 concrete based on DIC technology

Mechanical properties of polyvinyl alcohol-basalt hybrid fiber engineered cementitious composites with impact of elevated temperatures

Investigating the Mechanical Characteristics and Fracture Morphologies of Basalt Fiber Concrete: Insights from Uniaxial Compression Tests and Meshless Numerical Simulations

Deformation Damage and Energy Evolution of Basalt Fiber Reinforced Concrete under the Triaxial Compression