Study on crystal structure and phase transitions of polyamide 12 via wide-angle X-ray diffraction with variable temperature
Ruixin Dai,Miaoming Huang,Lili Ma,Wentao Liu,Suqin He,Hao Liu,Chengshen Zhu,Yujie Wang,Zhenya Zhang,Aihua Sun
DOI: https://doi.org/10.1007/s42114-020-00192-y
IF: 11.806
2020-11-23
Advanced Composites and Hybrid Materials
Abstract:Polyamide 12 (PA12) is a long carbon chain polyamide with plenty of excellent properties. In this work, PA12 samples were prepared in three ways: solution casting (α-crystal form at 30 °C and α + γ-crystal form at 40, 50, 60, and 80 °C, respectively), melt slow cooling (γ-crystal form), and melt quenching (γ-crystal form), which undergoes isothermal crystallization in the range from room temperature to the temperature close to the melting point. The crystallization behaviors, including the crystal transition, d-spacing, and crystallinity, upon heating and cooling were measured by the wide-angle X-ray diffraction (WAXD) from 30 to 235 °C. The results show that the α-crystal form gradually transforms into γ-crystal form during heating, indicating the occurrence of Brill transition. The γ-crystal form is stable below Tm, whereas the γ-crystal form can transform into γ-crystal form above 110 °C. Only γ-crystal form appears when cooling, and most of the crystallization has been completed before cooling to 170 °C. The investigation provides more theoretical supports of phase transitions in PA12 for deep understanding of the modification, optimization, and application.Graphical abstractTo investigate the crystallization behaviors of PA12, which were prepared in three ways: solution casting, melt slow cooling, melt quenching.
nanoscience & nanotechnology,materials science, composites