Microstructure and mechanical properties evolution of Ti-13Nb-13Zr alloy processed by ECAP-Conform and rotary swaging
Hui Qing Xu,Kun Xia Wei,Wei Wei,Jan Dzugan,Igor V. Alexandrov,Xu Long An,Dan Dan Wang,Xiang Kui Liu,Matej Daniel,David Hradil,Qiang Chen
DOI: https://doi.org/10.1016/j.jallcom.2023.172351
IF: 6.2
2023-10-01
Journal of Alloys and Compounds
Abstract:The evolution of the microstructure and properties of Ti-13 Nb-13Zr alloy was investigated for the materials states ranging from the solution treated (ST) state over the continuous equal channel angular pressing (ECAP-Conform) state to the states of the materials processed by combination of ECAP-Conform with rotary swaging (RS) multilevel deformation. In order to investigate microstructure features and mechanical properties for all considered material states, SEM, TEM , XRD and tensile and hardness tests were employed. The two-dimensional mismatch between α′, β, and α phases was calculated to evaluate the effect of the precipitation of the second phase. The results indicate that the microstructure of Ti-13 Nb-13Zr alloy transformed into majority of α′ martensite and a small percentage of residual metastable β m phase after ST. The grains were significantly refined, and a small part of α phase was precipitated during ECAP-Conform. As a result of ECAP-Conform + RS, the average grain size was refined from 34 μm after ST to 152 nm. The vast majority of the unstable phase was retained. Due to the ECAP-Conform + RS, the tensile strength increased to 1167.7 MPa while the elongation was 8.6%. The two-dimensional mismatch between α′, α, and β phases was 22.1%, which belongs to a semi-coherent relationship. The excellent mechanical properties were mainly attributed to the strengthening by α phase precipitation, dislocation strengthening, and grain refinement.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering