Novel Tri-rutile Ni0.5Ti0.5TaO4 Microwave Dielectric Ceramics: Crystal Structure Chemistry, Raman Vibration Mode, and Chemical Bond Characteristic In-Depth Studies

Xiaohui Wu,Yulan Jing,Yuanxun Li,Hua Su

DOI: https://doi.org/10.1021/acs.jpcc.2c03844

2022-01-01

Abstract:Here, a novel tri-rutile Ni0.5Ti0.5TaO4 ceramic configuration was first reported, and the sintering features, chemical bond theory, and microwave dielectric properties were systematically explored. Pure Ni0.5Ti0.5TaO4 ceramic with a tri-rutile structure was well sintered at 1275 degrees C with excellent microwave performance: epsilon(r) similar to 33.06, Q X f similar to 14,600 GHz, and tau(f) similar to 93.95 ppm/degrees C. Based on the P-V-L theory, the dielectric constant was mainly affected by the formation of Ta-O bonds (similar to 62%) due to the larger ionic polarization and bond susceptibility. The experimental dielectric constant (33.06) was comparable to the theoretical calculation (P-V-L: 35.11). The lattice energy was also dominated by the Ta-O bond (similar to 71%) and the intrinsic loss properties. The tau(f) was also affected by the [M1/M2O(6)] octahedral distortion. In addition, the relative density, grain size, and packing fraction also played a certain role in the microwave dielectric properties. Insights from the Raman spectroscopy revealed that the A(1g) mode dominated the Raman vibration at 699.44 cm(-1). These results were helpful to provide ideas for novel medium dielectric constant materials and contributed to the miniaturization of microwave electronic devices.