Novel Temperature Stable NiSnTa2O8 Microwave Dielectric Ceramics with Trirutile Structure

Enzhu Li,Qingyu Wen,Hongcheng Yang,Hongyu Yang,Qiu Yang,Shuren Zhang

DOI: https://doi.org/10.1016/j.ceramint.2019.11.069

IF: 5.532

2019-01-01

Ceramics International

Abstract:A novel low-loss and temperature stable NiSnTa2O8 ceramic with trirutile structure was prepared using traditional solid-state method. The structure-performance relationships were investigated by Rietveld refinement, chemical bond theory and far-infrared spectrum. The results show that the relative densities play a dominant role in the change of dielectric constant. Theoretical dielectric constant calculated via bond theory, Clausius-Mossotti equation and fitted result of far-infrared spectrum are close to experimental value. Ta-O bonds with greatest bond ionicity and bond energy have the primary contributions to dielectric polarizabilities and dielectric loss. The optimal microwave dielectric performances of NiSnTa2O8 ceramics were obtained: epsilon(r) similar to 21.04, Qxf similar to 31328 GHz and tau(f) = - 2.63 ppm/C at 1425 degrees C.