Influence of load ratio on fatigue life assessment of AZ31B magnesium alloy under different temperatures
Raj Kumar,Mohammad Mursaleen,G.A. Harmain
DOI: https://doi.org/10.1016/j.tafmec.2024.104557
IF: 4.374
2024-06-24
Theoretical and Applied Fracture Mechanics
Abstract:First ever fatigue crack growth experiments were conducted under various load ratios ( R = 0.1 to 0.8) at 300 K , and ( R = 0.1, 0.3, 0.5, and 0.7) at 327 K and 473 K , respectively, on AZ31B magnesium alloy. The results reveal that temperature-dependent variations in both fatigue crack growth rates and stress intensity factor ranges (Δ K ) across different load ratios. It was found that at relatively higher load ratio ( R = 0.8) leads to a lower Δ K = 8.0287 MPa√m and a lower load ratio ( R = 0.1) result in a higher Δ K = 15.5981 MPa√m, indicating that the material undergoes fatigue crack propagation at a higher level of stress intensity factor range at room temperature. A slower crack propagation was seen at higher load ratio ( R = 0.8), whereas lower load ratio ( R = 0.1) exhibits faster crack growth at 300 K . Similarly, crack growth generally increases at higher temperatures (i.e., 373 K and 473 K ). The fatigue life of the magnesium alloy AZ31B increased from 12,410 to 87,031 cycles at 300 K , 9,620 to 32,667 cycles at 373 K , and 9,140 to 30,143 cycles at 473 K as the load ratio increases. The average fatigue life decreases to 59 % and 63 % as the temperature is varied from 300 K through 373 K to 473 K . The fractographic and surface roughness carried out by field emission scanning electron microscopy and 3D-Profilometer respectively, illustrate that roughness of fracture surfaces correlates with an increase in the fatigue crack growth rate for a specific value of Δ K .
engineering, mechanical,mechanics