Irradiation Damage Independent Deuterium Retention in WMoTaNbV

Anna Liski,Tomi Vuoriheimo,Pasi Jalkanen,Kenichiro Mizohata,Eryang Lu,Jari Likonen,Jouni Heino,Kalle Heinola,Yevhen Zayachuk,Anna Widdowson,Ko-Kai Tseng,Che-Wei Tsai,Jien-Wei Yeh,Filip Tuomisto,Tommy Ahlgren

DOI: https://doi.org/10.3390/ma15207296

IF: 3.4

2022-01-01

Materials

Abstract:High entropy alloys are a promising new class of metal alloys with outstanding radiation resistance and thermal stability. The interaction with hydrogen might, however, have desired (H storage) or undesired effects, such as hydrogen-induced embrittlement or tritium retention in the fusion reactor wall. High entropy alloy WMoTaNbV and bulk W samples were used to study the quantity of irradiation-induced trapping sites and properties of D retention by employing thermal desorption spectrometry, secondary ion mass spectrometry, and elastic recoil detection analysis. The D implantation was not found to create additional hydrogen traps in WMoTaNbV as it does in W, while 90 at% of implanted D is retained in WMoTaNbV, in contrast to 35 at% in W. Implantation created damage predicted by SRIM is 0.24 dpa in WMoTaNbV, calculated with a density of 6.044×1022 atoms/cm3. The depth of the maximum damage was 90 nm. An effective trapping energy for D in WMoTaNbV was found to be about 1.7 eV, and the D emission temperature was close to 700 °C.