Flame Retardant and Toughening Modification of Poly(lactic acid) with Phenylhypophosphate Ionomer/Ammonium Polyphosphate
Cong Wu,Dan-dan Yang,Gang Wu,Si-chong Chen
DOI: https://doi.org/10.11777/j.issn1000-3304.2020.20161
2021-01-01
Acta Polymerica Sinica
Abstract:Poly(lactic acid) (PLA), as a kind of aliphatic polyester derived from biomass with excellent mechanical strength, biocompatibility and biodegradability, is a kind of green polymers with promising potential application. However, the application of PLA as a commodity polyester has been restricted dramatically because of its brittleness and flammability nature. It is still a great challenge to improve flame retardancy and toughness of PLA simultaneously by a simple blending method. In this work, copolymer ionomer (PCLA-PIU) was prepared by chain extension copolymerization of hydroxyl terminated poly(e-caprolactone) (PCL), PLA prepolymer and phenylhypophosphate, and then incorporated with ammonium polyphosphate (APP) for synergistic modification of PLA. The ionomer can act as a compatibilizer to enhance the dispersion of APP in PLA matrix because of its PLA segments and phenylhypophosphate groups. The SEM observation shows that the APP particles dispersed in PLA/PCLA-PIU/APP composite has significantly smaller size and uniform dispersity, compared to the PLA/APP20. The phenyl hypophosphate groups in the ionomer also has an excellent synergistic effect with APP for improving the flame-retardance of PLA. The flame-retardant properties and mechanism of the PLA and its composites were investigated by LOI, UL-94, Cone calorimeter test, SEM, EDS, Raman spectroscopy, etc. Compared with neat PLA and PLA/APP, the composite PLA/PCLA-PIU10/APP10 containing 10 wt% of PCLAP-IU and 10 wt% of APP10 achieves the V-0 rating in UL-94 burning test with limiting oxygen index (LOI) as high as 27.6%. The heat release rate and total heat release of PLA/PCLA-PIU10/APP10 are also reduced significantly to 254.9 kW/m(2) and 55.8 MJ/m(2), respectively. SEM and Raman analysis for char residues after Cone calorimeter test suggest PCLA-PIU and APP had synergistic effect on promoting charring of PLA, which result in compact char residue with high graphitization degree, therefore effectively improving the flame-retardant efficiency. Moreover, the toughness of PLA is improved effectively by the flexible PCL segments of ionomers, resulting in a PLA/PCLA-PIU/APP composite with improved flame retardancy and toughness simultaneously. The mechanical properties test results show that the toughness of the modified PLA (10.3 kJ/m(2) of PLA/PCLA-PIU10/APP10) is significantly improved compared to those of neat PLA (3.7 kJ/m(2)) and PLA/APP20 (2.5 kJ/m(2)).