In-Situ Synchrotron X-Ray Diffraction Study on Stress-Induced Martensite Transformation in Maraging Steel with High Strength and Good Ductility

Hu Li,Yong Liu,Weijiang Zhao,Bin Liu,Aki Tominaga,Takahisa Shobu,Daixiu Wei

DOI: https://doi.org/10.2139/ssrn.4193499

2022-01-01

SSRN Electronic Journal

Abstract:In this study, a cobalt-free Fe-18Ni-5Mo-2Cr-1.2Ti-0.4V maraging steel with high strength and good ductility was developed. The steel owned the combination of nanoscale precipitates within the martensite lath and the stress-induced martensitic transformation. The deformation behavior of the maraging steel was investigated by in-situ synchrotron X-ray diffraction. It was found that the dislocation density decreased sharply in the as-solution-annealed steel without the formation of precipitates, leading to a massive γ -austenite phase transformed into the α- martensite phase during tensile deformation. However, after aging treatment, the formation of high-density nanoscale Ni 3 (Ti, Mo) precipitates hindered the movement of dislocations, hence causing dislocation proliferation rapidly on loading. In addition, the pre-formed martensite in the aged steel was gradually transformed into a fresh orthogonal α′ phase when the applied stress was above ~876 MPa. Stress-induced martensitic transformation prevents crack generation and propagation. As a result, the steel had a strength up to ~1700 MPa and elongation of more than 11.7%.