Heterointerface Engineered NiFe(OH)x/Ni3S2 Electrocatalysts to Overcome the Scaling Relationship for Ultrahigh-Current-density Water Oxidation

Jiahao Zhang,Qiucheng Xu,Jingyu Wang,Yanjie Hu,Hao Jiang,Chunzhong Li

DOI: https://doi.org/10.1007/s40843-022-2190-7

2023-01-01

Abstract:Breaking the scaling relationship of water oxidation is the gateway to obtain an ultrahigh current density at a low potential for greatly improving the water electrolysis efficiency in industrial hydrogen production. Herein, we demonstrate a novel heterointerface engineered NiFe(OH) x /Ni 3 S 2 electrocatalyst to successfully circumvent the scaling relationship of the oxygen evolution reaction (OER), which significantly decreases the difference of the Gibbs free energy of HOO* and HO*(}ΔG hoo* –ΔG ho* ) from 3.20 to 2.38 eV. To achieve an ultrahigh current density of 2000 mA cm −2 , the NiFe(OH) x /Ni 3 S 2 electrocatalyst requires a small overpotential of 310 mV with an ultralow Tafel slope of 20.8 mV dec −1 . It can also steadily operate under 1000 mA cm −2 for over 100 h with insignificant activity loss, thus surpassing the state-of-the-art OER catalysts to date. A parallel catalytic mechanism has been disclosed to be responsible for the optimization of the reaction pathway, thus realizing the homogenization of multi-intermediate adsorption energy with extremely elevated OER catalytic performance at ultrahigh current densities. These findings could be a guidance in developing industrial-grade high-performance electrocatalysts for water splitting.