Abstract:The electrochemical behaviour for passivation of new alloy corrosion-resistant steel Cr10Mo1 immersed in alkaline solutions with different pH values (13.3, 12.0, 10.5, and 9.0) and chloride contents (0.2 M and 1.0 M), was investigated by various electrochemical techniques: linear polarization resistance, electrochemical impedance spectroscopy and capacitance measurements. The chemical composition and structure of passive films were determined by XPS. The morphological features and surface composition of the immersed steel were evaluated by SEM together with EDS chemical analysis. The results evidence that pH plays an important role in the passivation of the corrosion-resistant steel and the effect is highly dependent upon the chloride contents. In solutions with low chloride (0.2 M), the corrosion-resistant steel has notably enhanced passivity with pH falling from 13.3 to 9.0, but does conversely when in presence of high chloride (1.0 M). The passive film on the corrosion-resistant steel presents a bilayer structure: an outer layer enriched in Fe oxides and hydroxides, and an inner layer, rich in Cr species. The film composition varies with pH values and chloride contents. As the pH drops, more Cr oxides are enriched in the film while Fe oxides gradually decompose. Increasing chloride promotes Cr oxides and Fe oxides to transform into their hydroxides with little protection, and this is more significant at lower pH (10.5 and 9.0). These changes annotate passivation characteristics of the corrosion-resistant steel in the solutions of different electrolyte.

Unraveling Electrochemical Performance of a 10crmo Steel in Alkaline Concrete Pore Solutions with Red Mud and Ground Granulated Blast-Furnace Slag

Role of Red Mud in Natural Passivation and Chloride-Induced Depassivation of Reinforcing Steels in Alkaline Concrete Pore Solutions

Spontaneous Passivation and Passivity Breakdown of a Novel 10crmo Steel in Simulated Seawater Concrete Pore Solutions

Passivation and Pitting Corrosion Behavior of a Novel Alloy Steel (00Cr10MoV) in Simulated Concrete Pore Solution

Synergistic Effect of Red Mud and Fly Ash on Passivation and Corrosion Resistance of 304 Stainless Steel in Alkaline Concrete Pore Solutions

Enhanced Passivity of Reinforcing Steel in Cementitious Materials with Thermally-Activated Red Mud

Passive Behaviour of New Alloy Corrosion Resistant Steel Cr10Mo1 in Simulating Concrete Pore Solutions with Different Chloride Contents

Pore Solution Chemistry of Calcium Sulfoaluminate Cement and Its Effects on Steel Passivation

Passivation Behavior of Steel in Novel Low-Carbon Binders with Belitic Calcium Sulfoaluminate Cement

Beneficial and Detrimental Impacts of Molybdate on Corrosion Resistance of Steels in Alkaline Concrete Pore Solution with High Chloride Contamination

Passive Behavior of New Alloy Corrosion Resistant Steel Cr10Mo1 in Chloride-containing Environment

Passive behaviour of alloy corrosion-resistant steel Cr10Mo1 in simulating concrete pore solutions with different pH

Electrochemical Responses of Carbon Steel in Ordinary Portland Cement Blended with Calcium Sulfoaluminate Cement

Electrochemical Behaviour of a Novel Alloy Steel in Alkali-Activated Slag Mortars

Passivation and Depassivation of HPB335 Carbon Steel in Simulated Concrete Pore Solution

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study

Enhanced Corrosion Resistance of Reinforcing Steels in Simulated Concrete Pore Solution with Low Molybdate to Chloride Ratios

Passivation Characteristics Of Alloy Corrosion-Resistant Steel Cr10mo1 In Simulating Concrete Pore Solutions: Combination Effects Of Ph And Chloride

Experimental and ReaxFF MD Study on Cr10Mo Steel Passivation in Simulated Concrete Pore Solutions

Passivation and depassivation properties of Cr–Mo alloyed corrosion-resistant steel in simulated concrete pore solution

Passive Film Modification by Concrete Carbonation: Re-visiting a Corrosion-Resistant Steel with Cr and Mo