Effect of Tensile Deformation on Microstructure and Corrosion Resistance of High Nitrogen Austenitic Stainless Steels
Zheng Chun,Liu Jiabin,Jiang Laizhu,Yang Cheng,Jiang Meixue
DOI: https://doi.org/10.11900/0412.1961.2021.00504
IF: 1.797
2022-01-01
ACTA METALLURGICA SINICA
Abstract:Nitrogen-alloyed austenitic stainless steel QN1803 (2.0%Ni-3.5%Ni) has been developed to replace the conventional 304 stainless steel (8%Ni). Both the microstructure and the corrosion resistance of both types of stainless steels in the annealed state have been extensively studied, whereas those in the cold strained state have not been studied sufficiently. The aforementioned stainless steels often undergo cold forming processes during industrial applications, such as straightening, leveling, and bending, etc., which may lead to the changes of microstructure and corrosion resistances as well as the performance. In this study, the tensile tests were performed with different tensile strains for both nitrogenalloyed QN1803 and the conventional 304 stainless steels. The microstructure and strengthening, as well as the toughening mechanisms were investigated using EBSD, XRD, and TEM. The corrosion resistance and its mechanism under different tensile strains were evaluated and analyzed via electrochemical workstation, acid corrosion tests, OM, and SEM. Notably, the microstructures of both QN1803 and 304 stainless steels are changed from dislocation plugging to a' martensite with the increase in tensile strain. The yield strength of QN1803 stainless steel is 26% higher, while its elongation is 6.6% lower than that of 304 stainless steels, respectively. This could be attributed to both the higher nitrogen content and the lower transition temperature of 50% martensite induced by 30% strain (M-d30) for QN1803 stainless steel as compared with that for 304 stainless steel. As a result, the volume fraction of the strain-induced martensite for QN1803 stainless steel under tensile strain is lower, leading to the lower toughening effect than that of 304 stainless steel. Interestingly, the experiments show that the tensile strain has a minor effect on the intergranular corrosion whereas noticeably negative effect on both the pitting and the sulfuric acid corrosion resistances of both stainless steels. Not surprisingly, 304 stainless steel undergoes a more remarkable decrease in both the pitting and the sulfuric acid corrosion resistances with the increase in tensile strain as compared with QN1803 stainless steel. This could be well understood since martensite could lead to the destruction or deterioration of the passive film on the stainless steel surface, producing an unstable dissolution-generation state during corrosion, thus reducing the corrosion resistance after tensile deformation. In conclusion, the yield strength is enhanced, ductility is slightly impaired, and both the pitting and the sulfuric acid corrosion resistances under tensile deformation are improved by nitrogen alloying. Based on these technical advantages, together with the nickel saving effect, QN1803 stainless steel has been applied in various industrial areas, such as building, construction, and home appliance, etc.