Directed Synthesis of an Unusual Uniform Trimetallic Hydrogen Evolution Catalyst by a Predesigned Cobalt-Bipy Modified Bivanadyl Capped Polymolybdate

Xinyu Che,Qiong Wu,Sumin Hu,Guangning Wang,Haijun Pang,Weize Sun,Huiyuan Ma,Xinming Wang,Lichao Tan,Guixin Yang

DOI: https://doi.org/10.1016/j.jssc.2022.123403

IF: 3.3

2022-01-01

Journal of Solid State Chemistry

Abstract:Heterometallic sulfides are one type of non-precious metal, environmentally friendly and high-activity electro-catalysts for electrocatalytic hydrogen evolution reaction (HER). Nevertheless, different metallic reagents generally possess distinct nucleation reaction rates. Therefore, there is a still big challenge currently to obtain uniform heterometallic sulfide catalysts especially for trimetallic catalysts. In this work, a new crystalline poly-oxometalate (POM)-based coordination polymer [Co-III(bipy)(3)](2){[Co-II(bipy)(2)(H2O)](2) [(HPMo4Mo8O40)-Mo-V-O-VI((VO)-O-IV)(2)]} [(HPMo10Mo2O40)-Mo-V-O-VI((VO)-O-IV)(2)] (abbreviated to Co-bipy-PMo12V2) was prepared, where the bipy is abbreviation of 2,2'-bipy. In the polymer, the POM anions exhibit novel bivanadyl capped Keggin cluster structures and they are further modified cobalt-bipy subunits to form a supramolecular framework. Subsequently, the polymer was used as a "pre-assembled platform" for the preparation of heterometallic sulfides in the presence of thiourea under hydrothermal conditions. Consequently, an unusual high dispersed trimetallic sulfides were in-situ coupled on carbon cloth (CC) substrate to give birth to a novel self-supported CoS2-MoS2-VS2-CC composite electrode. The composite was characterized by PXRD, XPS, SEM, etc. Also, a series of tests on the electrochemical behavior of the composite electrode were carried out using a three-electrode system to investigate its electrocatalytic HER performance. The overpotential and Tafel slope of the electrode can approach to 152 mV and 107 mV dec(-1), respectively. Moreover, the polarization curves of the CoS2-MoS2-VS2-CC electrode completely overlapped before and after 1000 cycles of voltammetric tests in 1.0 M KOH electrolyte. The chrono-current method reveals that the CoS2-MoS2-VS2-CC electrode can maintain stability electrocatalytic activity at a current density of 10 mA cm(-2) for at least 24 h. Thus, the CoS2-MoS2-VS2-CC catalyst possesses both superior electrocatalytic HER performance and long-term durability. This study provides a facile route for the rational design and preparation of high dispersed trimetallic sulfide catalysts.