Abstract:We report here a generalized synthesis of various crystalline mesoporous metal oxides including CeO2, Cr2O3, Fe2O3, SnO2, Ce0.5Zr0.5O2, TiO2, Al2O3 and ZrO2 from the self-assembly of a basic poly 4-vinylpyridine (P4VP) template with various metal precursors based on their strong acid–base interaction under high temperature (180 °C) hydrothermal conditions. Using the typically crystalline mesoporous metal oxide of CeO2, after removing the template by calcination at 550 °C and loading with various transition metal oxides such as MnOx, various transition metal oxide functionalized crystalline mesoporous CeO2 (MnOx/P4VP–CeO2) were obtained. X-ray diffraction (XRD) patterns show that the resulting mesoporous metal oxides exhibit a high degree of crystallinity, and the transition metal oxides active sites have been successfully loaded into these samples. N2 sorption–desorption isotherms, SEM images show that the resulting crystalline mesoporous metal oxides, such as CeO2, have a large BET surface area (94 m2 g−1) and abundant mesopores, which exhibit monolithic morphology with crystal sizes ranging from 5 to 15 μm, giving a uniform pore size centered at 5 nm. XPS spectra show that the active sites such as MnOx exhibit the phases of MnO2 and Mn2O3 in P4VP–CeO2. H2-TPR curves show that MnOx/P4VP–CeO2 exhibits decreased reductive temperatures of both active sites of the MnOx and P4VP–CeO2 supporter when compared with the samples reported previously. More importantly, MnOx/P4VP–CeO2 exhibits much better catalytic activities and good recyclability for catalyzing the oxidation of benzene than that of MnOx loaded commercially crystalline CeO2, which will be very important for their wide applications for VOCs removal in industry.

Bimodal Mesoporous CeO2–ZrO2-based Materials Prepared by PMMA Nanosphere Assisted Co-Precipitation and Its Thermal Stability

Generalized and High Temperature Synthesis of a Series of Crystalline Mesoporous Metal Oxides Based Nanocomposites with Enhanced Catalytic Activities for Benzene Combustion

Preparation and characterization of high specific surface area Ce 0.5Zr0.5O2 mixed oxide

Preparation of ceria-zirconia by modified coprecipitation method and its supported Pd-only three-way catalyst

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Effect of Synthesis Condition on Properties of Ce0.67zr0.33o2 Mixed Oxides and Its Application in Pd-Only Three-Way Catalysts

Effect of Preparation Method on the Surface and Redox Properties of Ce0.67zr0.33o2 Mixed Oxides

Preparation of Ce0.67Zr0.33O2 mixed oxides as supports of improved Pd-only three-way catalysts

Preparation of Ultrafine Ce-Zr-Ba Mixed Oxide Powder with High Surface Area

Oxygen Storage Capacity of Pt-, Pd-, Rh/CeO2-Based Oxide Catalyst

Structure and Oxygen Storage Capacity of Pr-doped Ce0.26Zr0.74O2 Mixed Oxides

The support effect on PdO/Ce 0.7 Zr 0.3 Ba 0.1 O 2.1 and CuO/Ce 0.7 Zr 0.3 Ba 0.1 O 2.1 catalysts

Preparations and Characterizations of New Mesoporous ZrO2 and Y2O3-stabilized ZrO2 Spherical Powders

Structure Properties and OSC Performance of Pr-Ce-Zr Mixed Oxides

Structural studies of mesoporous ZrO$_{2}$-CeO$_{2}$ and ZrO$_{2}$-CeO$_{2}$/SiO$_{2}$ mixed oxides for catalytical applications

Synthesis and Characterization of Thermally Stable Mesostructured Sulfated Zirconia by a Novel Sulfate-Assisted Alcohothermal Route

Synthesis of a homogeneous CeO2–ZrO2-Al2O3 composite material by a novel hydrothermal assisted precipitation method

The Support Effect on Pdo/Ce0.7zr0.3ba0.1o2.1 and Cuo/Ce0.7zr0.3ba0.1o2.1 Catalysts

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

Cerium–zirconium mixed oxide synthesized by sol-gel method and its effect on the oxygen vacancy and specific surface area