Mechanism of Calcium Stearate Deteriorating the Wear Resistance of UHMWPE: Structure–property Relationship

Liu Zhipeng,Du Yue,Li Jiangshan,Kang Da,Ye Chunlin,Zhao Shicheng

DOI: https://doi.org/10.1007/s10965-022-03283-0

IF: 3.061

2022-01-01

Journal of Polymer Research

Abstract:The flowability of Ultra-high molecular weight polyethylene (UHMWPE) is very poor so flow modification is needed to improve its processing efficiency, but flow modification could significantly deteriorate its wear resistance. To solve this technical problem, it is necessary to recognize the reasons why flow modifiers deteriorate the wear resistance of UHMWPE. In current research, influence of calcium stearate (CaSt) which is a commonly used flow modifier on the wear resistance of UHMWPE was investigated, the experimental results showed that a small amount of CaSt (0.5wt%) could significantly deteriorate the wear resistance of UHMWPE (11%). Subsequently, the effect of CaSt on the three-phase structure (amorphous, crystalline and interphase) of UHMWPE was investigated to explain why CaSt deteriorates the wear resistance of UHMWPE in terms of structure–property relationship. The study of crystallization and melting behavior indicates that the incorporation of CaSt makes the matrix produce more well-formed crystals thus increasing the hardness of the matrix, and the increase in hardness can alleviate the degree of abrasive wear. The study of the amorphous region found that CaSt has a unique disentanglement effect, which reduces the degree of entanglement of molecular chains of the matrix, and the reduction of the degree of entanglement deteriorates the shear resistance of the matrix, thus aggravating the shear damage of the sample during the wear process. Meanwhile, the disentanglement effect of CaSt can also improve the recrystallization ability of the matrix, reducing the interphase of the matrix thus making the matrix more susceptible to structural damage during the wear process. Furthermore, the incorporation of CaSt significantly reduces the heat resistance of the matrix, which makes the wear resistance of the matrix deteriorate more caused by the friction heat during the wear process. This paper can provide theoretical guidance to solve the problem of severe degradation of wear resistance after flow modification of UHMWPE and provide inspiration for the structural design of other wear-resistant materials.