Abstract:The all-composite sandwich structure with the honeycomb core is a lightweight and high-strength structure with broad application scenarios. The face sheet and honeycomb core of the proposed all-composite sandwich structure in this work are composed of carbon-fiber-reinforced polymer (CFRP) composites. The mechanical response and damage mechanism of the all-composite sandwich structure under out-of-plane quasi-static compression and out-of-plane impact are studied by numerical methods. The refined finite element models of the sandwich structures are built on the ABAQUS/Explicit platform. The micromechanics of failure (MMF) theory based on physical component failure is used to describe the intralaminar damage mechanism of the face sheet and honeycomb core, and the mixed-mode exponential cohesive zone model (ECZM) is utilized to simulate the initiation and evolution of interlayer damage. In addition, the cohesive contact approach is adopted to capture the debonding failure at the face-sheet/core. The numerical results show that the all-composite sandwich structure has the characteristics of large structural stiffness and strong energy absorption ability. The failure mechanism of the all-composite sandwich structure under compression is mainly matrix damage and delamination of the honeycomb core, with buckling and folding in appearance. Under out-of-plane impact, matrix damage and delamination arise on the upper sheet, little damage is observed on the lower sheet, and the delamination damage morphology tends to be circular with increasing impact energy. In addition, the interface failure of the upper-sheet/core is more than that of the lower-sheet/core. In addition, the matrix damage near the impact center of the honeycomb core tends to be consistent with the delamination contour, and a small amount of fiber failure is also observed, which manifests as a collapse morphology of the impact area. The research results enrich the understanding of the mechanical behavior of all-composite sandwich structures with honeycomb cores and provide theoretical support for their potential applications.

Compression Performance of Composite Honeycomb Sandwich Structures with Prefabricated Defects

Damage sensitivity studies of composite honeycomb sandwich structures under in-plane compression and 4-point bending: experiments and numerical simulations

Effect of Defect on the Compressive Response of Sandwich Structures with Carbon Fiber Pyramidal Truss Cores

Numerical Studies on Failure Mechanisms of All-Composite Sandwich Structure with Honeycomb Core under Compression and Impact Loading Conditions

Investigation on the Compressive Mechanical Properties of Ultra-Thick CFRP Laminates

Experimental study on compression properties of composite aluminum honeycomb sandwich structures

Compressive response and failure mode of glass fiber reinforced polyimide composite honeycomb with cell wall defects

Analysis of Honeycomb and Sandwich Structure Compression Property and the Damage of Double Cell Wall

Deformation behaviors of defective aluminum honeycomb sandwich panels subjected to in-panel compressive loading: an experimental study with mirror-assisted multi-view DIC

Study on Aluminum Honeycomb Sandwich Panels with Random Skin/Core Weld Defects

Residual Compressive Strength of Aluminum Honeycomb Sandwich Structures with CFRP Face Sheets after Low-velocity Impact

In-plane compressive response of composite sandwich panels with local-tight honeycomb cores

Investigation of failure behavior in honeycomb sandwich panel containing interfacial debonding

Dynamic Compression Failure Mechanisms and Dynamic Effects of Integrated Woven Sandwich Composites

Macroscopic Response of Carbon-Fiber Pyramidal Truss Core Panel Taking Account of Local Defect

Mechanical Properties Test and Failure Analysis of Composite Foam Sandwich Structure in Ramp-Down Zone

Mechanical behaviors and failure modes of sandwich cylinders with square honeycomb cores under axial compression

Experimental Study on Compression Failure of Composite Laminates with Prefabricated Surface Cracks

On Impact Damage and Repair of Composite Honeycomb Sandwich Structures

Damage Resistance of Honeycomb Sandwich Composites under Low-Energy Impact

Numerical and experimental investigation of pre-damaged composite stiffened panel under axial compression