Anisotropic mechanical responses and plastic deformation mechanisms of cadmium telluride under indentations

Chao Xu,Weilu Zhang,Mingdong Hu,Jing Zhang,Zhe Lang,Pengwei Li,Huaping Liu,Pei Wang,Chunmei Liu
DOI: https://doi.org/10.1007/s00339-022-05873-7
2022-01-01
Applied Physics A
Abstract:Molecular dynamic simulations were performed to investigate the indentations of CdTe crystal on (100), (110) and (111) surfaces. We found that the incipient plasticity, hardness, elastic recovery ratio and the structural evolution of CdTe during the indenting process depend strongly on the orientation of the indented surfaces due to the anisotropic nature of CdTe. The obtained load–displacement curves showed abrupt drops at critical indentation depths, indicating the occurrence of incipient plasticity. We found that the (001) plane yields first during the indenting process, followed by (110) plane, and the (111) plane yields last. For all the indented planes of CdTe, the incipient plasticity should be resulted from the nucleation and propagation of 1/2 < 110 > dislocations, which is consistent with the results from both experiments and the calculations of the generalized stacking fault energy. We found that the dislocation distribution under the indented (110) plane shows a twofold rotation symmetry, while those under the indented (111) and (001) planes show three- and fourfold rotation symmetry, respectively. The temperature effect on the indentation responses and structural evolution were also studied. This paper will not only answer the question about the orientation-dependent indentation responses of CdTe crystals, but also reveal the dislocation activities under the indentations in real time. The results of this paper are generally applicable to CdTe single-crystal systems and may provide reference data to improve the design and ultimately performance of the related CdTe-based devices.
What problem does this paper attempt to address?