Simple Glycerol-Assisted and Morphology-Controllable Solvothermal Synthesis of Lithium-Ion Battery-Layered Li 1.2 Mn 0.54 Ni 0.13 Co 0.13 O 2 Cathode Materials
Jing Fang,Hao An,Furong Qin,Hongqi Wang,Chao Chen,Xiaohan Wang,Yinghui Li,Bo Hong,Jie Li
DOI: https://doi.org/10.1021/acsami.0c16755
2020-12-07
Abstract:High-performance lithium-rich-layered oxide is regarded as a promising candidate for lithium-ion battery (LIB) cathode materials because of its outstanding high specific capacity. Despite in-depth research over the past decade, there are still a number of serious problems limiting its commercialization. Here, we report a simple morphological design and size-controllable material preparation strategy to enhance the electrochemical performance of LIB cathode materials. We use a simple solvothermal method to obtain a carbonate precursor material with different morphologies by adjusting the solvent ratio of the system, which will be conveniently formed into Li<sub>1.2</sub>Mn<sub>0.54</sub>Ni<sub>0.13</sub>Co<sub>0.13</sub>O<sub>2</sub> by calcination. Moreover, further relation between the morphology and electrochemical performance of cathode materials is systematically investigated. The microsphere cathode material with suitable size exhibits superior electrochemical performances among all samples in terms of initial reversible capacity (280.4 mA h g<sup>–1</sup> at 0.1 C) and cycle performance (87.67% retention after 200 cycles at 1 C). Even at 5 C, a high discharge capacity of 150.8 mA h g<sup>–1</sup> can be obtained. In addition, this work provides a feasible and effective approach to controllable synthesis of stable structures and high-performance oxide electrode materials for LIBs.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c16755?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c16755</a>.Internal morphology of secondary microparticle; XRD pattern of all carbonate precursors; EDX analysis of final products for samples LR-0, LR-4, and LR-6; comparison of mean size and tap density for all samples; SEM image and EDS mapping of Mn, Co, and Ni elements for LR-0, LR-2, LR-4, and LR-6 precursors; SEM images of the electrode after 100 cycles at 1 C; SEM images of pristine electrodes and cycled electrodes; and charge/discharge curves for the electrode (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c16755/suppl_file/am0c16755_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology