Microstructure evolution and mechanical properties of NbHfTiVCx novel refractory high entropy alloys with variable carbon content
Shutian Tao,Wei Jiang,Wei Zhang,Haochen Qiu,ShuaiShuai Wu,Shengli Guo,Baohong Zhu
DOI: https://doi.org/10.1016/j.jallcom.2022.166986
IF: 6.2
2022-12-20
Journal of Alloys and Compounds
Abstract:A refractory high entropy alloy (RHEA) NbHfTiV was selected as the master alloy and carbon element was introduced to synthesize the novel NbHfTiVCx RHEAs (x = 0, 0.1, 0.2, 0.3), which perform outstanding strength and excellent ductility simultaneously. Phase identification, microstructure evolution, and mechanical properties were systematically analyzed. The results show that the primary MC-type carbides and nano-precipitate carbides are generated in the BCC matrix phase with the addition of carbon. The primary carbides evolve from solid spheroid (x = 0.1) to sandwich-like pattern (x = 0.2, 0.3), and grain size is significantly refined from 537 μm (x = 0) to 25 μm (x = 0.3). Compressive tests show that the yield strength increases from 958 MPa to 1115 MPa, and the fracture mechanism is changed from ductile fracture to ductile and brittle mixed fracture with carbon content increasing. Meanwhile, the atomic size mismatch and elastic mismatch of the matrix phase reduce with carbon content increasing, which could decrease the lattice distortion degree and soften the matrix phase.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering