The effect of multiple factors on the synthesis of mullite whiskers based on the S-L-S mechanism and the comparison of strengthening performance
Nan Yang,Ruoyu Zhang,Tian Qin,Yuqing Zhang,Xuemin Wei,Ziqing Wang,Zhaojie Feng,Mingchao Wang
DOI: https://doi.org/10.1016/j.jallcom.2024.174947
IF: 6.2
2024-05-25
Journal of Alloys and Compounds
Abstract:s Mullite whiskers were synthesized based on the S-L-S growth mechanism at high temperatures using nano-alumina sol and nano-silica sol as the main materials and ammonium molybdate tetrahydrate as an additive. The effects of the silica-aluminum ratio, addition of ammonium molybdate catalyst, sintering temperature, and sintering time on the generation of mullite whiskers were systematically investigated to determine the optimal synthesis conditions. It was shown that the best raw material formulation was (3Al 2 O 3 ·2.2SiO 2 ) 8 (MoO 3 ) 2 , which minimized the mass loss of precursor powder at 0–1200°C, with only 23.62%. The mullite whiskers generated by sintering for 1–3 h maintained good microforms without agglomeration. The optimal growth conditions were 1300°C sintering for 1 h. The resulting mullite whiskers grew along the [240] direction and had the largest aspect ratios up to 10.2–14.3. The highest generation rate was up to 94.5 wt% with a grain size of 81.6 nm. The BET surface area was 2.308 m 2 /g and the pore size was 5.44 nm. The mass loss at 0–1200°C was the least, only 1.32%, with good thermal stability. In addition, the effects of (xAl 2 O 3 ·ySiO 2 ) 8 (MoO 3 ) 2 (x:y=3:1.8, 3:2, 3:2.2) whiskers treated at 1300°C on the APSB adhesive and MSABS adhesive bonding were investigated in this paper, it was clear that whiskers with x:y=3:2.2 had the best enhancement effect. For APSB adhesive strength could be increased by up to 55% and the fracture displacement by 2.42 times. For MSABS adhesives, the strength could be increased by up to 47% and the fracture displacement by 1.49 times.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering