Abstract:Polydimethylsiloxane (PDMS) is usually used to obtain favorable performances of waterborne polyurethane (WPU) such as higher hardness, exceptional thermal stability and lower interfacial tension. However, there is always a problem that waterborne polyurethane (WPU) often performs weak tensile strength, lower tenacity and brittle property at room temperature when polydimethylsiloxane (PDMS) is embedded into the backbone of polyurethane. The study aims to address the problem by constructing dual crosslinking structure, namely introducing trimethylolpropane as an intramolecular crosslinking agent into prepolymers and then adding waterborne polycarbodiimide (SK-400) as a post-crosslinking agent in order to further enlarge the degree of crosslinking and mainly make up for the shortcoming that mechanical property decreases when polydimethylsiloxane (PDMS) was inserted into molecule chains. Initially a novel inner-crosslinking prepolymer (SiWPU) comprising polydimethylsiloxane need to be synthesized successfully by inserting trimethylolpropane into prepolymers. Then the sample SiWPU-3 was picked out as a matrix resin and dropwise added polycarbodiimide (SK-400) as a post-crosslinking agent into the matrix resin (C–SiWPU). As pH was gradually lowering following the evaporation of triethylamine in the emulsion (C–SiWPU), carboxyl groups (COOH) in prepolymers started to react with SK-400 (NCN) to form twofold crosslinking structure. When 0%, 2%, 4%, 6%, and 8 wt% of waterborne polycarbodiimide (SK-400) was incorporated into the solution, the tensile strengths are 47.8 MPa, 57.7 MPa, 65 MPa, 57.6 MPa and 54.5 MPa and the elongation at break 732%, 756%, 798%, 707% and 700%. The crosslinking density of SiWPU-3 without the addition of waterborne polycarbodiimide (SK-400) is 3.86 × 10−3 mol/cm3. As 6 wt% of waterborne polycarbodiimide (SK-400) was added into the emulsion of SiWPU-3, the crosslinking density of C–SiWPU-6 (6 wt% SK-400) is 6.19 × 10−3 mol/cm3. The films show excellent extensibility and exceptional tenacity. Hence, the emulsion is able to be applied in leather industry.

Preparation, Mechanical and Thermal Properties of Polydimethylsiloxane Coating for Synthetic Leathers

Synthesis, characterization and lubricating effect of long chain branched polydimethylsiloxane-g-polyethylene copolymers

Mechanical properties and thermal stability of ambient-cured thick polysiloxane coatings prepared by a sol-gel process of organoalkoxysilanes

Ambient-curable polysiloxane coatings: structure and mechanical properties

Enhanced Mechanical and Adhesive Properties of PDMS Coatings Via In-Situ Formation of Uniformly Dispersed Epoxy Reinforcing Phase

Preparation and Research of Hydrophobic PDMS/Nano-SiO2 Modified SiO2 Coating

The Preparation and Properties Study of Polydimethylsiloxane-Based Coatings Modified by Epoxy Resin

The Preparation of a Novel Moisture-Curing Silicone Conformal Coating

Evaluation of mechanical properties and hydrophobicity of room‐temperature , moisture‐curable polysilazane coatings

Assessment of the Physical, Mechanical, and Tribological Properties of PDMS Thin Films Based on Different Curing Conditions

Pickering Emulsion Approach for Fabrication of Waterborne Cross-Linkable Polydimethylsiloxane Coatings with High Mechanical Performance

Effect of PDMS Viscosity and Additive Amount of Curing Agent Solution on the Mechanical Properties of PDMS Fouling Release Coating

Synthesis of waterborne polyurethane by inserting polydimethylsiloxane and constructing dual crosslinking for obtaining the superior performance of waterborne coatings

Microstructure and Thermal Properties of Silyl‐terminated Polycaprolactone–polysiloxane Modified Epoxy Resin Composites

Preparation and Surface Properties of Silicone-Modified Polyester-Based Polyurethane Coats

Preparation of Fluorosilicone Random Copolymers with Properties Superior to Those of Fluorosilicone/Silicone Polymer Blends

Preparation and properties of polysiloxane modified fluorine-containing waterborne polyurethane emulsion

Preparation and Properties of PED-TDI Polyurethane-Modified Silicone Coatings

Fabrication and Characterization of Polysiloxane/polyacrylate Composite Latexes with Balanced Water Vapor Permeability and Mechanical Properties: Effect of Silane Coupling Agent

Preparation and Properties of Polyurethane Coatings Modified by Polysilazane

Preparation and properties of waterborne siloxane-containing polyurethane for moisture permeable textile coating