Gas permeation and selectivity of polysulfone/carbon non-woven fabric membranes with sponge and finger-like structures
Alaa Mohamed,Samy Yousef,Simona Tuckute,Andrius Tonkonogovas,Arūnas Stankevičius
DOI: https://doi.org/10.1016/j.psep.2023.01.055
2023-01-28
Process Safety and Environmental Protection: Transactions of the Institution of Chemical Engineers, Part B
Abstract:This research aims to investigate the effect of supporting polysulfone (PSF) membranes with different pore structures (sponge "SP" and finger "FP") by non-woven carbon fibers (CF) on their gas permeability and selectivity for different gas mixtures (H 2 /CO 2 , H 2 /N 2 , and H 2 /CH 4 ) to avoid the lower mechanical strength of the commercial membranes. The thickness of the PSF layer was modified during the preparation process using a phase inversion approach. The impact of the support CF fabric and different pore structures on the mechanical, chemical, thermal, permeability, and selectivity characteristics of the fabricated membranes were examined. The results revealed a strong incorporation between PSF and the fabric, resulting in enhanced pores, increased porosity and higher roughness. The FP membrane's structure was found to have a smaller pore size of 56 nm, higher porosity (73.6%), surface roughness (44 nm) and higher strength (15.7 MPa) but less thermal stability (−36%) compared to the SP structure. Moreover, the SP structure exhibited higher gas permeability, particularly for H 2 , with improvements of 32% for H 2 and CO 2 , 25% for CH 4 , and 10% for N 2 . Furthermore, the PSF/CF membrane with SP structure exhibited higher selectively with 15.8%, 26.9%, and 14.4% improvements for H 2 /CO 2 , H 2 /N 2 , H 2 /CH 4 , respectively, compared to FP membranes. These results suggest that CF fabric has great potential as a membrane substrate and PSF/CF membranes with SP structures have high potential for use in the H 2 gas separation process in harsh environments.