Abstract:The ceramic core plays an important role in the preparation of aero-engine hollow blades, as it can directly determine the precision and pass rate of the cooling passage in the blade cavity. Sufficient high-temperature bending strength, high open porosity, and low sintering shrinkage are the main requirements for qualified ceramic cores. In order to prepare qualified ceramic cores with complex structures, in-situ mullite-reinforced Al2O3-based ceramic cores were successfully prepared using vat photopolymerization 3D printing technology. The in-situ synthesis of mullite was designed through thermodynamic analysis. The influence mechanisms of the sintering temperature and doping amount of fused silica on the open porosity, sintering shrinkage, and bending strength of the core were systematically investigated. With an increase in the sintering temperature and doping amount of fused silica, the porosity of the in situ mullite-reinforced ceramic core decreased. Sintering shrinkage increased with an increase in the sintering temperature and doping amount of fused silica. The cores containing 20 wt% fused silica showed the smallest sintering shrinkage. The bending strength increased with an increase in the sintering temperature and the doping amount of fused silica. A core doped with 20 wt% fused silica had the highest bending strength at 1773.15 K. Furthermore, 20 wt% fused silica doping, sintered at 1673.15 K, can be used to prepare in-situ mullite enhanced Al2O3-based cores with the best comprehensive properties. This core has a higher open porosity (40%), suitable bending strength of 25 MPa (at 1773.15 K), and lower sintering shrinkage in the Z direction. The significance of this study lies in the regulation of in-situ mullite generation and viscous flow in solid-liquid sintering by adjusting the doping amount of fused silica and the sintering process, and this opens up new pathways by the coordinated regulation of strength, open porosity, and sintering shrinkage of 3D printed ceramic cores.

Enhanced Comprehensive Properties of Stereolithography 3D Printed Alumina Ceramic Cores with High Porosities by a Powder Gradation Design

Microstructure and properties evolution of silicon-based ceramic cores fabricated by 3D printing with stair-stepping effect control

Additive manufacturing of Al2O3 ceramic core with applicable microstructure and mechanical properties via digital light processing of high solid loading slurry

In-situ Y3Al5O12 enhances comprehensive properties of alumina-based ceramic cores by vat photopolymerization 3D printing

Microstructure and mechanical properties of 3D-printed nano-silica reinforced alumina cores

3D Printing of Silica-Based Ceramic Cores Reinforced by Alumina with Controlled Anisotropy

The influence of sintering procedure and porosity on the properties of 3D printed alumina ceramic cores

3D Printed Ceramic Slurries with Improved Solid Content Through Optimization of Alumina Powder and Coupling Agent

Innovative ceramic paste for stereolithography additive manufacturing alumina core applied in turbine blade casting

Anisotropy management on microstructure and mechanical property in 3D printing of silica-based ceramic cores

Fabrication of Al2O3 ceramic cores with high porosity and high strength by vat photopolymerization 3D printing and sacrificial templating

Balancing Flexural Strength and Porosity in DLP-3D Printing Al2O3 Cores for Hollow Turbine Blades

Effect of Sintering Temperature on Microstructure and Properties of 3D Printing Polysilazane Reinforced Al 2 O 3 Core

Silica strengthened alumina ceramic cores prepared by 3D printing

High solid loading, low viscosity stereolithography 3D printing ceramic cores slurry

Enhanced 3D printed Al2O3 core via in-situ mullite

Additive manufacturing of low-shrinkage alumina cores for single-crystal nickel-based superalloy turbine blade casting

Controlled anisotropy in 3D printing of silica-based ceramic cores through oxidization reaction of aluminum powders

Enhanced 3D Printed Alumina Ceramic Cores Via Impregnation

High-performance 3D-printed Al2O3 cores for low-temperature sintering

Enhanced high-temperature dimensional accuracy by fibers in silica ceramic cores prepared through vat photopolymerization 3D printing