Effect of Aluminothermic Reduction Conditions on the Phase Structure and Chemical Composition of Al-Ti-Ce Master Alloy

Li Sen,Gao Feng,Shen Dongdong,Long Wenyuan,Li Xinsheng,Wang Kaituo,Wang Youbin,Toyohisa Fujita,Wei Yuezhou
2022-01-01
Rare Metal Materials and Engineering
Abstract:Al-Ti-Ce master alloy was prepared by aluminothermic reduction of TiO2 and CeO2 in Na3AlF6-NaCl-KCl electrolytic system. The effects of reaction time, reaction temperature, electrolytic composition (mass fraction of Na3AlF6) and K2TiF6 dosage on the phase structure and chemical composition of Al-Ti-Ce master alloy were studied. The experimental results show that there are only three phases in the Al-Ti-Ce master alloy, which are alpha-Al, Al3Ti and Ti2Al20Ce, at the range of process parameters used in each experiment, and the optimal single-factor parameters in preparing Al-Ti-Ce master alloy by aluminothermic reduction are as follows: reaction time 90 min, reaction temperature 850 degrees C, content of Na3AlF6 40wt%, K2TiF6 dosage 20mol%. The results of thermodynamic analysis further show that the main several chemical reactions proposed in this study are feasible on the checked experimental conditions.
What problem does this paper attempt to address?