Abstract:Selection of an appropriate membrane material for guided bone regeneration (GBR) is still ongoing among resorbable and nonresorbable membranes with different characteristics. The major problem with nonresorbable membranes is the inevitable secondary surgery, while resorbable polymer membranes have limitations in providing sufficient mechanical support during the bone repair period due to premature loss of mechanical strength. Pure magnesium foil has been evaluated to explore its feasibility as a resorbable GBR membrane. It exhibited better mechanical properties, whereas poor formability and fast degradation rate were noted. In light of this, pure zinc membrane was developed as a pilot research in this paper. We designed three types of pure zinc membranes: pure Zn without pores, pure Zn with 300 pm diameter and 1000 pm diameter pores, and pure titanium without pores as a control. The mechanical property, in vitro immersion tests, and MC3T3-E1 cell viability assays were tested. Moreover, in vivo behaviors of three type zinc membranes were evaluated by using a rat calvarial critical-sized bone defect model. The experimental results indicated that pure Zn membrane with 300 pm pores showed the most favorable osteogenic capability, comparable to that of titanium membrane without pores. Therefore, considering appropriate degradation rate, adequate mechanical maintenance, and profitable osteogenic capacity, metallic pure zinc is believed to be a promising candidate for barrier membranes in GBR therapy for bone regeneration, and its mechanical property can be enhanced with further alloying. Statement of Significance Metallic element zinc plays a pivotal role in the growth and mineralization of bone tissues. As a pilot research, three type of guided bone regeneration (GBR) membranes were developed in the present work: pure Zn without pores, pure Zn with 300 mu m-diameter and 1000 pm-diameter pores respectively. The mechanical property, in vitro immersion tests and MC3T3-E1 cell viability assays were tested, with pure titanium without pores as a control, thereafter the in vivo performance were evaluated by using a rat calvarial critical-sized bone defect model. It indicated that pure Zn membrane with 300 mu m pores showed the most favorable osteogenic capability, comparable to that of titanium membrane control, and is believed to be a promising material candidate as barrier membrane in GBR therapy for bone regeneration. (C) 2020 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Fabrication and Characterization of A Zn-0.5Fe Alloy Membrane by Powder Metallurgy Route for Guided Bone Regeneration

Appropriately adapted properties of hot-extruded Zn–0.5Cu–xFe alloys aimed for biodegradable guided bone regeneration membrane application

Mechanical Properties, Microstructure, Degradation Behavior, and Biocompatibility of Zn-0.5Ti-0.5Fe and Zn-0.5Ti-0.5Mg Guided Bone Regeneration Barrier Membranes Prepared Using a Powder Metallurgy Method

A Pure Zinc Membrane with Degradability and Osteogenesis Promotion for Guided Bone Regeneration: in Vitro and in Vivo Studies

Degradation Behavior, Transport Mechanism and Osteogenic Activity of Mg–Zn–RE Alloy Membranes in Critical-Sized Rat Calvarial Defects

ZnP‐Coated Zn1Cu0.1Ti Membrane with High Strength‐Ductility, Antibacterial Ability, Cytocompatibility, and Osteogenesis for Biodegradable Guided Bone Regeneration Applications

Highly plastic Zn-0.3Ca alloy for guided bone regeneration membrane: Breaking the trade-off between antibacterial ability and biocompatibility

In Vitro and in Vivo Evaluations of Mg-Zn-Gd Alloy Membrane on Guided Bone Regeneration for Rabbit Calvarial Defect

Improved mechanical, degradation, and biological performances of Zn-Fe alloys as bioresorbable implants

An Extracellular Matrix-like Surface for Zn Alloy to Enhance Bone Regeneration.

Biodegradable Zn-Cu-Fe Alloy as a Promising Material for Craniomaxillofacial Implants: An in vitro Investigation into Degradation Behavior, Cytotoxicity, and Hemocompatibility

Development of biodegradable Zn-Mn-Li and CaP coatings on Zn-Mn-Li alloys and cytocompatibility evaluation for bone graft

An in vitro and in vivo study of biodegradable Zn–Cu–Li alloy with high strength and ductility fabricated by hot extrusion combined with room-temperature ECAP

Microstructure, Mechanical Properties, and in Vitro Corrosion Behavior of Biodegradable Zn-1Fe-xMg Alloy

Bioactive Zn-0.6Cu thin sheet for craniofacial bone repair: In vitro and in vivo evaluations

Fabrication and Properties of a Biodegradable Zn-Ca Composite

Enhanced Biocompatibility and Osteogenic Property of Biodegradable Zn-0.5Li Alloy through Calcium–Phosphorus Coating

Processing Optimization, Mechanical Properties, Corrosion Behavior and Cytocompatibility of Additively Manufactured Zn-0.7Li Biodegradable Metals.

Research on corrosion behavior and biocompatibility of a porous Mg-3%Zn/5%β-Ca3(PO4)2 composite scaffold for bone tissue engineering

Evaluation of As‐extruded Ternary Zn–Mg–Zr Alloys for Biomedical Implantation Material: in Vitro and in Vivo Behavior

Utilizing biodegradable alloys as guided bone regeneration (GBR) membrane: Feasibility and challenges