Abstract:This study investigates the alternative of replacing noble metals by base metals as catalysts for selective hydrogenation of polyunsaturated hydrocarbons. Nickel catalysts are active for this type of reaction, but poorly selective. However, former calculations anticipated that Ni–Zn alloys could have higher selectivity to alkenes than monometallic Ni depending on the Ni/Zn atomic ratio in the alloy. In this contribution, Ni–Zn alloy nanoparticles supported on TiO2 are synthesized as catalysts for selective hydrogenation of acetylene and butadiene. The designed catalysts with 0.5 wt% Ni loading and various Ni/Zn nominal ratios are prepared by deposition–precipitation with urea (DPU). STEM-HAADF imaging coupled with EDS analysis reveals that Ni–Zn bimetallic particles are formed after reduction treatment at 450 °C. Alloying Ni with Zn leads to a slight increase in the average particle size and a broadening of the size distribution compared to monometallic Ni. However, the average Ni/Zn atomic ratio measured by EDS in the bimetallic particles is always higher than the nominal one, which could be due to Zn evaporation under the beam. The results of acetylene hydrogenation show that although the catalytic activity is slightly reduced after alloying Ni with Zn, the selectivity to ethylene is enhanced from 50% up to 85%, at the expense of the formation of oligomers (coupling products). However, the bimetallic Ni–Zn catalysts suffer from progressive deactivation in this reaction. During butadiene hydrogenation performed in the presence of an excess of propene, the bimetallic Ni–Zn/TiO2 catalysts are significantly more stable, with a high and constant selectivity to butenes (> 95%), compared with Ni/TiO2, which deactivates rapidly in the first hours. Some hypotheses concerning the observed differences in catalytic stability are discussed.

Selective Hydrogenation of 1,3-Pentadiene on Mono- and Bimetallic Nickel and Palladium Catalysts

Ligand-controlled Fabrication of Core-Shell PdNi Bimetallic Nanoparticles As a Highly Efficient Hydrogenation Catalyst

Design Strategies and Structure-Performance Relationships of Heterogeneous Catalysts for Selective Hydrogenation of 1,3-Butadiene

Efficient Selective Hydrogenation of Terminal Alkynes over Pd–Ni Nanoclusters Encapsulated Inside S-1 Zeolite

Bimetallic Ni–Zn/TiO2 catalysts for selective hydrogenation of alkyne and alkadiene impurities from alkenes stream

Hydrotalcite-Based Bimetallic PdNi Catalysts with High Sulfur Tolerance for the Hydrogenation of Dicyclopentadiene Resin

Selective Alkyne Semi‐Hydrogenation by PdCu Nanoparticles Immobilized on Stereocomplexed Poly(lactic acid)

Chemoselective Hydrogenation of Nitrobenzyl Ethers to Aminobenzyl Ethers Catalyzed by Palladium–nickel Bimetallic Nanoparticles

Theoretical study the influence of partial substitute noble metal Pd/Ag of PdAg-based catalyst by non-noble metal Ni/Cu for 1,3-Butadiene hydrogenation

Dendrimer-Encapsulated Pd Nanoparticles, Immobilized in Silica Pores, as Catalysts for Selective Hydrogenation of Unsaturated Compounds

50 Ppm of Pd Dispersed on Ni(OH)2 Nanosheets Catalyzing Semi-Hydrogenation of Acetylene with High Activity and Selectivity

Regulation of a Ni3Sn2 intermetallic catalyst using highly dispersed Pd species to boost propyne semi-hydrogenation

An Ab Initio Study of Size-Selected Pd Nanocluster Catalysts for the Hydrogenation of 1-Pentyne

Investigating the Long-Term Kinetics of Pd Nanoparticles Prepared from Microemulsions and the Lindlar Catalyst for Selective Hydrogenation of 3-Hexyn-1-ol

Tuning hydrogenation chemistry of Pd-based heterogeneous catalysts by introducing homogeneous-like ligands

Highly Selective and Stable Isolated Non-Noble Metal Atom Catalysts for Selective Hydrogenation of Acetylene

Pdti Alloys As an Excellent Catalyst for Semi-Hydrogenation Reactions

Selective Hydrogenation Of Phenylacetylene Over Pd-Cu/Gamma-Al2o3 Catalysts

Molecular Understanding of Enyne Hydrogenation over Palladium and Copper Catalysts

Activation and Spillover of Hydrogen on Sub‐1 Nm Palladium Nanoclusters Confined Within Sodalite Zeolite for the Semi‐Hydrogenation of Alkynes