Abstract:Background Intraorbital implantation of coralline porous hydroxyapatite (CHA) is a favorable cosmetic method after enucleation.However,the low degree of vascularizatiou in implant results in implant infection and exposure.Studies showed that a collagen composite sponge treated by basic fibroblast growth factor (bFGF/ collagen composite sponge) can promote angiogenesis.However,whether bFGF/collagen composite sponge improves the vascularization of CHA implants is unclear.Objective This study was to investigate the accelerating effect of bFGF collagen composite sponge on vascularization of orbital implant made of CHA using 99Tcm-methylene diphosphate (MDP) scan.Methods Forty-five New Zealand rabbits were randomly assigned to 3 groups.Evisceration of eyeball was performed on the left eyes of rabbits,and naked CHA,collagen composite sponge wrapped CHA and bFGF/collagen composite sponge wrapped CHA were implanted into the orbit respectively in 3 groups.99Tcm-MDP of 3 mCi was injected in the rabbits via ear vein in 2,4,6,8 and 12 weeks,and the vascular enhancement intensity on implants was observed 3 hours after injection.The ratio of average radioactive count from the area of interest with the same size between the left eyes and the right eyes was calculated.The implants were extracted for histopathological examination in the 12 weeks.Results As the lapse of postoperative time,the inflammation response gradually disappeared and no exposure of implants was seen during the 12-week duration.A similar vascular development strength was found in the area of interest among the 3 groups 2 weeks after surgery.However,the vascular development was significantly enhanced in the left eyes compared the right eyes from 4 to 6 weeks,with the highest intensity in the 8th week in the naked CHA group and collagen composite sponge wrapped CHA group.In the bFGF/ collagen composite sponge wrapped CHA group,the strongest image was in the 6th week after operation.The ratios of average radioactive count between the left eyes and the right eyes were significantly higher in the bFGF/collagen somposite sponge wrapped CHA group compared with the naked CHA group and collagen composite sponge wrapped CHA group (all at P＜0.05),and ratios of average radioactive count of the collagen composite sponge wrapped CHA group was significantly higher than that of the naked CHA group (all at P＜0.05).New blood vessels ingrowed toward the center of the implants through the coralline porous under the optical microscope.Conclusions Both bFGF (20 μg)/collagen composite sponge and collagen composite sponge can accelerate the ingrowth of vessel in the CHA,but the promoting effect of bFGF collagen composite sponge is prominent.

Copper-Doped Bioactive Glass/Poly (Ether-Ether-Ketone) Composite as an Orbital Enucleation Implant in a Rabbit Model: An In Vivo Study

Synergistic Effect of Copper-Containing Mesoporous Bioactive Glass Coating on Stimulating Vascularization of Porous Hydroxyapatite Orbital Implants in Rabbits

Next-generation Finely Controlled Graded Porous Antibacterial Bioceramics for High-Efficiency Vascularization in Orbital Reconstruction

Engineering Self-Antimicrobial Implants with Precision Pore Architectures for Personized Orbital Reconstruction

Rational Design and Fabrication of Porous Calcium-Magnesium Silicate Constructs That Enhance Angiogenesis and Improve Orbital Implantation.

Biological Activity of a Vascular Endothelial Cell-Hydroxyapatite Orbital Implant Complex: an Experimental Study.

Evaluation of bFGF collagen composite sponge promoting vascular ingrowth in orbital implantation by 99Tcm-MDP scan

Facile Fabrication of Elastic, Macro-Porous, and Fast Vascularized Silicone Orbital Implant.

An Effective Osteogenesis Cryogel Γ-Pga/hema/peg Served As Rabbit Orbital Bone Defects Scaffolds

Tuning zinc content in wollastonite bioceramic endowing outstanding angiogenic and antibacterial functions beneficial for orbital reconstruction

Reconstruction of an Orbital Defect in Rabbits Using a Silk Fibroin-Bone Microparticle Complex

Bioinspired adhesive polydopamine-metal-organic framework functionalized 3D customized scaffolds with enhanced angiogenesis, immunomodulation, and osteogenesis for orbital bone reconstruction

Simultaneous Enhancement of Vascularization and Contact-Active Antibacterial Activity in Diopside-Based Ceramic Orbital Implants.

Influence of Cu Doping in Borosilicate Bioactive Glass and the Properties of Its Derived Scaffolds

Copper-doped borosilicate bioactive glass scaffolds with improved angiogenic and osteogenic capacity for repairing osseous defects.

Fibrovascularization of high-density porous polyethylene implanted into the rabbit's orbit

A comparative in vitro and in vivo analysis of the impact of copper substitution on the cytocompatibility, osteogenic, and angiogenic properties of a borosilicate bioactive glass

PLGA- Membrane Wrap for the Implantation of Hydroxyapatite Orbital Implants: an Animal Model

Bioactive Copper-Doped Glass Scaffolds Can Stimulate Endothelial Cells in Co-Culture in Combination with Mesenchymal Stem Cells

3D printing of Cu-doped bioactive glass composite scaffolds promotes bone regeneration through activating the HIF-1 and TNF- pathway of hUVECs

Development of Biodegradable Bioactive Glass Ceramics by DLP Printed Containing EPCs/BMSCs for Bone Tissue Engineering of Rabbit Mandible Defects