Abstract:Although highly dispersed Au catalysts with Au nanoparticles (NPs) of a few nanometers in diameter are well-known for their high catalytic activity for several oxidation and reduction reactions already at rather low temperatures for almost 30 years, central aspects of the reaction mechanism are still unresolved. While most studies focused on the active site, the active Au species, and the effect of the support material, the most crucial step during oxidation reactions, the activation of molecular oxygen and the nature of the resulting active oxygen species (Oact), received more attention just recently. This is topic of this Account, which focuses on the formation, location, and nature of the Oact species present on metal oxide supported Au catalysts under typical reaction conditions, at room temperature and above. It is mainly based on quantitative temporal analysis of products (TAP) reactor measurements, which different from most spectroscopic techniques are able to detect and quantify these species even at the extremely low concentrations present under realistic reaction conditions. Different types of pulse experiments were performed, during which the highly dispersed, realistic powder catalysts are exposed to very low amounts of reactants, CO and/or O2, in order to form and reactively remove Oact species and gain information on their formation, nature, and the active site for Oact formation. Our investigations have shown that the active oxygen species for CO oxidation on Au/TiO2 for reaction at 80 °C and higher is a highly stable atomic species, which at 80 °C is formed only at the perimeter of the Au-oxide interface and whose reactive removal by CO is activated, but not its formation. From these findings, it is concluded that surface lattice oxygen represents the Oact species for the CO oxidation. Accordingly, the CO oxidation proceeds via a Au-assisted Mars-van Krevelen mechanism, during which surface lattice oxygen close to the Au NPs is removed by reaction with CO, resulting in a partially reduced TiO2 surface, which is subsequently reoxidized by O2. We demonstrate that this is the dominant reaction pathway for Au catalysts based on reducible metal oxides in general, at typical reaction temperatures, while for less active Au catalysts based on nonreducible metal oxides, this reaction pathway is not possible and the remaining activity must arise from another pathway, most probably a Au-only mechanism. At lower reaction temperature, reactive removal of Oact becomes increasingly inhibited, leading to a change in the dominant reaction pathway.

Activation of Oxygen Species on Ag/CoAlO Catalysts to Promote CO Oxidation by Enhancing Metal‐Support Interactions

Enhanced CO oxidation performance over hierarchical flower-like Co 3 O 4 based nanosheets via optimizing oxygen activation and CO chemisorption

Nano-sized Ag rather than single-atom Ag determines CO oxidation activity and stability

Oxyhydroxide Species Enhances CO2 Electroreduction to CO on Ag Via Coelectrolysis with O2

Chemisorbed Superoxide Species Enhanced the High Catalytic Performance of Ag/Co 3 O 4 Nanocubes for Soot Oxidation

Reduction-oxidation Pretreatment Enhanced Catalytic Performance of Co3O4/Al2O3 over CO Oxidation

Promoting effect of reduction-oxidation strategy on the Co3O4/γ-Al2O3 catalysts for propane total oxidation

Hollow-Structural Ag/Co3O4 Nanocatalyst for CO Oxidation: Interfacial Synergistic Effect

Heterostructure-strengthened metal-support interaction of single-atom Pd catalysts enabling efficient oxygen activation for CO and VOC oxidation

CO Oxidation over Alumina-Supported Copper Catalysts

Great activity enhancement of Co3O4/γ-Al2O3 catalyst for propane combustion by structural modulation

Activation of molecular oxygen and the nature of the active oxygen species for CO oxidation on oxide supported Au catalysts

A First-Principle Study of Synergized O2 Activation and CO Oxidation by Ag Nanoparticles on TiO2(101) Support.

Catalytically active ceria-supported cobalt-manganese oxide nanocatalysts for oxidation of carbon monoxide.

Constructing Ag Single Atoms and Nanoparticles Co‐Decorated CoO(O)H as Highly Active Electrocatalyst for Oxygen Evolution Reaction under Large Current Density

Preferential carbon monoxide oxidation on Ag/Al-SBA-15 catalysts: Effect of the Si/Al ratio

Investigation of catalytic methane oxidation over Ag/Co2MOx (M = Co, Ni, Cu) catalysts with varying interfacial electron transfer

Efficient CO Oxidation using Co3O4−CeO2 Nanoparticles Supported on Resin–Based Spherical Activated Carbon with Controllable Oxygen Species

Structure-induced Hollow Co3O4 Nanoparticles with Rich Oxygen Vacancies for Efficient CO Oxidation

Ag Anchored Atomically Around Nanopores of Porous Co(OH)2 for Efficient Bifunctional Oxygen Catalysis

Pt/MOx/SiO2, Pt/MOx/TiO2, and Pt/MOx/Al2O3 Catalysts for CO Oxidation