Synthesis and characterization of phase pure and Mg-modified AgZnVO 4 microwave dielectrics for high-frequency ULTCC applications
Cheng-Liang Huang,Yi-Lun Hsieh,Tsung-Hsien Hsu,I-Chun Ling
DOI: https://doi.org/10.1016/j.jallcom.2023.169890
IF: 6.2
2023-04-03
Journal of Alloys and Compounds
Abstract:A novel low-loss and ultra-low temperature sinterable microwave dielectric material, AgZnVO 4 , was systematically investigated for the first time. The material exhibited a monoclinic structure with a space group P21/n, obtained by conventional solid-state processing. The material also showed combined microwave dielectric properties of ε r = 10.3, Q×f = 42,000 GHz, and τ f = –9.2 ppm/°C for specimens sintered at 540 °C. The partial substitution of Mg for Zn in the Ag(Zn 1−x Mg x )VO 4 ceramics effectively improved the densification and reduced the dielectric loss of the ceramics. X-ray diffraction patterns revealed a single solid solution phase of Ag(Zn 1−x Mg x )VO 4 . The relative density, dielectric polarizability, packing fraction, lattice energy, and bond valence of the samples were calculated. An excellent combination of the microwave dielectric properties was obtained for Ag(Zn 0.97 Mg 0.03 )VO 4 ceramic sintered at 540 °C: ε r = 10.6, Q×f = 52,000 GHz, and τ f = –10 ppm/°C. Additionally, the ceramic exhibited good chemical compatibility with aluminum electrodes, indicating great potential for ultra-low temperature co-fired ceramics (ULTCC) applications, particularly in the microwave and millimeter wave regions.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering