Abstract:This article presents the physical and mechanical properties of geopolymer concrete with lightweight artificial aggregate. A research experiment where the influence of fly ash–slag mix (FA-S), as part of a pozzolanic additive, on the properties of geopolymers was carried out and the most favorable molar concentration of sodium hydroxide solution was determined. The values of three variables of the examined properties of the geopolymer lightweight concrete (GLC) were adopted: X1—the content of the pozzolanic additives with fly ash + flay ash–slag (FA + FA-S) mix: 200, 400 and 600 kg/m3; X2—the total amount of FA-S in the pozzolanic additives: 0, 50 and 100%; X3—the molarity of the activator NaOH: (8, 10 and 12 M). In order to increase the adhesion of the lightweight artificial aggregate to the geopolymer matrix, the impregnation of the NaOH solution was used. Based on the obtained results for the GLC’s compressive strength after 28 days, water absorption, dry and saturated density and thermal conductivity index, it was found that the most favorable parameters were obtained with 400 kg/m3 of pozzolanic additives (with 50% FA-S and 50% FA) and 10 NaOH molarity. Changes in the activator’s concentration from 8 to 10 M improved the compressive strength by 54% (for a pozzolana content of 200 kg/m3) and by 26% (for a pozzolana content of 600 kg/m3). The increase in the content of pozzolanic additives from 200 to 400 kg/m3 resulted in a decrease in water absorption from 23% to 18%. The highest conductivity coefficient, equal to 0.463 W/m·K, was determined, where the largest amount of pozzolanic additives and the least lightweight aggregate were added. The structural tests used scanning electron microscopy analysis, and the beneficial effect of impregnating the artificial aggregate with NaOH solution was proved. It resulted in a compact interfacial transition zone (ITZ) between the lightweight aggregate and the geopolymer matrix because of the chemical composition (e.g., silica amount), the silica content and the alkali presoaking process.

Effects of plastic coating on the physical and mechanical properties of the artificial aggregate made by fly ash

Study on the Effect of Fly Ash and Polycarboxylic Acid Water Reducer on the Properties of Recycled Concrete

Synthesis and Properties of Fly Ash Geopolymer with Dyeing Sludge

Impacts of Alkaline Washing Pretreatment on Municipal Solid Waste Incineration Fly Ash (MSWI FA) and Resulting Geopolymers

Analysis of the Impact and Mechanism of Polyacrylate-Based Composite Paste on the Performance of Recycled Aggregate

Sustainable Cement Mortar with Recycled Plastics Enabled by the Matrix-Aggregate Compatibility Improvement

Recent advances in artificial aggregate production

Effect of Rice Husk Ash on Properties of Slag Based Geopolymer Pastes

Cleaner geopolymer prepared by co-activation of gasification coal fly ash and steel slag: durability properties and economic assessment

Effects of air-entraining agent and polypropylene fiber on the mechanical properties, autogenous shrinkage, and fracture properties of fully recycled aggregate concrete

Preparation and properties of geopolymer containing phosphoric acid-activated fly ash and mechanically-milled kaolinite: Experiments and density function theory

Low-carbon wet-ground fly ash geopolymer activated by single calcium carbide slag

Factors affecting the property of open-cell fly ash-based porous geopolymer via replica method

Geopolymer Concrete with Lightweight Artificial Aggregates

Effects of Aggregate Micro Fines (AMF), Aluminum Sulfate and Polypropylene Fiber (PPF) on Properties of Machine-Made Sand Concrete

An efficient approach for sustainable fly ash geopolymer by coupled activation of wet-milling mechanical force and calcium hydroxide

In-Depth Insight into the Effects of Steel Slag and Calcium Hydroxide on the Properties of a Fly Ash-Red Mud Geopolymer

An Investigation of Mechanical Properties of Concrete by Applying Sand Coating on Recycled High-Density Polyethylene (HDPE) and Electronic-Wastes (E-Wastes) Used as a Partial Replacement of Natural Coarse Aggregates

The Influence of Different Aggregates on the Physico-Mechanical Performance of Alkali-Activated Geopolymer Composites Produced Using Romanian Fly Ash

Recycling air-cooled blast furnace slag in fiber reinforced alkali-activated mortar