Abstract:Polymer bonded explosive (PBX) is a composite consisting of the polymer binder and embedded explosive particles, along with a large number of the particle/binder interfaces as the third constituent. The particle volume fraction is often higher than 90%. In the present work, a visco-elastic constitutive model, an elastic visco-plastic constitutive model and a bilinear cohesive contact relationship model are implemented into the numerical manifold method (NMM) program, an open source code programmed with C language, to describe the deformations of the polymer binder, the explosive particles and the particle/binder interfaces, respectively. The fracturing of the polymer binder and explosive particles is described based on the maximum tensile stress and the Mohr-Coulomb criteria. Three categories of initial defects, including the initial interfacial debonding, initial voids in the polymer binder, and initial micro-cracks in the explosive particles, are considered in the PBX meso-structures under both uniaxial tensile and compressive conditions. The tension-compression asymmetry, the influence of the initial defects on the meso-structure failure modes/patterns and the macroscopic effective tensile/compressive strength of PBXs are investigated. The factors that cause the differences between the NMM results and other numerical or experimental results are analyzed and discussed. This work enables and proves the NMM to be an robust numerical tool for further simulation studies of the mechanical performances of PBXs, as well as other particle-filled composites, at the meso-scale.

Numerical Simulation of PBX-9501 Crack Generation Under Tensile Loading

Numerical Analysis of the Damage and Failure Behavior of Polymer-Bonded Explosives Using Discrete Element Method

Simulations of Meso-Scale Deformation and Damage of Polymer Bonded Explosives by the Numerical Manifold Method

Experimental analysis and multi-scale simulation of the fracture behavior of polymer-bonded explosives based on the dynamic notched semi-circular bend method

Modelling Microstructural Deformation and the Failure Process of Plastic Bonded Explosives Using the Cohesive Zone Model

Meso-scale Failure Simulation of Polymer Bonded Explosive with Initial Defects by the Numerical Manifold Method

A Micromechanical Model for Predicting Combined Damage of Particles and Interface Debonding in PBX Explosives

Numerical Modeling of Crack Growth in Polymer-Bonded Explosive with Cavity Subject to Compression

Numerical Mesoscopic Investigations of Dynamic Damage and Failure Mechanisms of Polymer Bonded Explosives

The Dynamic Mechanical Behaviour and the Statistical Crack Mechanics Model for a Polymer-bonded Explosive

Mechanical Behavior of a PBX Substitute Material under Static and Dynamic Loading

Meso-structure Construction and Effective Modulus Simulation of PBXs

Fracture behavior of PBX simulation subject to combined thermal and mechanical loads

Mechanical Property and Damage Evolution of Polymer-Bonded Explosive Substitute under Biaxial Compression

Experimental Study on the Localized Deformation and Damage Behavior of Polymer-Bonded Explosive Simulant under Cyclic Compression

Numerical Simulations of Microcrack-Related Damage and Ignition Behavior of Mild-Impacted Polymer Bonded Explosives

Numerical Simulations of the Damage Evolution for Plastic-Bonded Explosives Subjected to Complex Stress States

Deformation and Failure of Polymer Bonded Explosives under Diametric Compression Test

On the Tension-Induced Microcracks' Nucleation in a PBX Substitute Material under Impact Compression Loading

Investigation on Fracture Behavior of Polymer-Bonded Explosives under Compression Using a Viscoelastic Phase-Field Fracture Method

Damage Constitutive Model of PBX Explosive and Its Engineering Application