Treatment on Co/GNs Composites with Ce(NO 3 ) 3 Aqueous Solution for Selective Multiple-Broadband Electromagnetic Wave Absorption Performance

Qin Zhaohui,Wang Chunyu,Zhong Bo,Ma Yuanyuan,Chen Weidong,Li Xingji,Zhang Peng

DOI: https://doi.org/10.1557/s43578-022-00505-5

2022-01-01

Abstract:In this study, the Co/GNs composites was successfully synthesized by a facile hydrothermal method, and under moderate conditions, CeO2–Co/GNs composites were prepared by a simple way of stirring H2O2 at 45 ℃ for 2 h. This work finds that by adjusting the concentration ratio of Ce3+ to Co/GNs, the dielectric loss, magnetic loss, and good impedance matching greatly enhance the electromagnetic (EM) wave absorption capacity. Meanwhile, CeO2–Co/GNs composites exhibit the strongest reflection loss of − 40.91 dB with a thickness of 4.9 mm. It is worth noting that even for the low frequencies of the S (2–4 GHz) and X (8–12 GHz) bands, RL has the strongest intensity, superior to most of Co-based absorbers that have been reported so far. Therefore, the CeO2–Co/GNs composites can be expected to have strong absorption strength, selectable bandwidth, including S (2–4 GHz), C (4–8 GHz), X (8–12 GHz), and Ku (12–18 GHz) bands, ensuring it an attractive EM wave absorber.