Intermetallics in Ni–Al Binary Alloys: Liquid Structural Origin
Zhao Yimeng,Cao Saichao,Zeng Long,Xia Mingxu,Jakse Noel,Li Jianguo
DOI: https://doi.org/10.1007/s11661-022-06910-z
2022-01-01
Abstract:Nickel aluminum (Ni–Al) intermetallics with various lattice structures become emerging multi-functional materials as next-generation superalloys, catalyzers, and even coating materials, but the liquid structural origin for the intermetallic formation is still a mystery. Here, the atomic structure difference of the intermetallic precursor liquids is investigated using in-situ high-energy X-ray diffraction, reverse Monte Carlo simulations at 9 °C above the liquidus temperature as well as ab initio molecular dynamics. It is noted that Ni10Al90, Ni20Al80, and Ni35Al65 alloys, corresponding to the quasi-crystalline phase (Q-phase) formation related to Al3Ni, Al3Ni2, and NiAl intermetallics, have less icosahedral-like clusters in the liquids comparing with the other two face-centered cubic (FCC) forming alloys (Ni2Al98 and Ni74.5Al24.5). Strong interconnection of central atoms among the icosahedral-like clusters was observed in the three Q-phases-related liquids, stimulating the intermetallic formation. The pre-peaks found in the total X-ray structure factors are closely related to the Al3Ni, Al3Ni2, and NiAl intermetallics in terms of the bond lengths. FCC forming liquids either on the high Al or on the high Ni side did not show any pre-peak phenomenon instead. The findings in this work ignite the investigation of the liquid structural origin for the intermetallics and extend the understanding of the atomic structure evolution in solidification.