Abstract:The direct synthesis of light olefins from syngas via Fischer-Tropsch synthesis reaction is a promising technology for direct synthesis of olefins from syngas. The key is to improve the selectivity of light olefins through the regulation of product distribution. In this work, the hydrophobic Fe@Si catalyst was prepared by room temperature solid state methodStober-silylation method, and then the catalyst was combined with SAPO-34 molecular sieves with different contents to prepare Fe@Si/S-34 composite catalysts. The effects of SAPO-34 molecular sieve content on the physicochemical properties of the catalysts were investigated by X-ray diffraction, scanning electron microscopy, N-2 adsorption-desorption, NH3 temperature programmed desorption and water contact angle measurement. The results showed that the content of SAPO-34 molecular sieve has significant influence on the surface area, pore volume, acidity and hydrophobicity of the catalysts. With the increase of SAPO-34 molecular sieve content, the specific surface area and total pore volume of the catalyst increased, the weak acid and medium-strong acid sites increased, and the hydrophobicity weakened. The catalytic performance evaluation results showed that the Fe@Si/S-34 composite catalyst decomposed C5+ hydrocarbons into light hydrocarbons, significantly reduced the selectivity of C5+ products and increased the selectivity of C2 similar to C4 hydrocarbons. Appropriate SAPO-34 molecular sieve could significantly improve the selectivity of C2 similar to C-4 olefins. When the mass ratio of Fe@Si catalyst to SAPO-34 is 2, the C-2 similar to C-4 olefin selectivity of Fe@Si/S-34 catalyst is the highest, the conversion of CO is 80.0%, the selectivity of CO2 in the product is 8.9%, and the selectivity of C-2 similar to C-4 olefins is 31.1%. In this study, the hydrophobicity of Fe@Si catalyst and the cracking activity of SAPO-34 molecular sieve for C5+ hydrocarbon were coupled together to inhibit the water-gas shift (WGS) reaction, reduce the CO2 selectivity and obtain higher C-2 similar to C-4 olefin selectivity, which provided a new strategy for the development of catalysts for Fischer-Tropsch synthesis to olefins.

Boosting CO2 Hydrogenation Performance for Light Olefin Synthesis over GaZrOx Combined with SAPO-34

Bifunctional Catalyst Ga2O3-mZrO2/SAPO-34 for CO2 Hydrogenation: Ga2O3-mZrO2 Improving Light Olefins

Zn promoted GaZrOx ternary solid solution oxide combined with SAPO‐34 effectively converts CO2 to light olefins with low CO selectivity

Bifunctional Catalysts Composed of Low Silicon‐content SAPO‐34 Nanosheets and in 2 O 3 /zro 2 with Improved Performance for CO 2 Hydrogenation

Preparation of Fe@Si/S-34 Catalysts and Its Catalytic Performance for Syngas to Olefins

Tuning CO2 Hydrogenation to Light Olefin Selectivity via Cu/Zn/Zr Supported on Modified SAPO‐34

Bifunctional catalyst consisting of In-modified GaZrOx ternary solid solution oxide and SAPO-34 for efficiently converting CO 2 into light olefins

Highly Active Catalytic CO2 Hydrogenation to Lower Olefins via Spinel ZnGaOx Combined with SAPO-34

CO 2 hydrogenation to light olefins over Zn–Zr/support-SAPO-34: comparison of different supports

GamCrOx/H-SAPO-34(F), a highly efficient bifunctional catalyst for the direct conversion of CO2 into ethene and propene

Carbon Dioxide Hydrogenation to Light Olefins over ZnO-Y2O3 and SAPO-34 Bifunctional Catalysts

Highly selective hydrogenation of CO 2 to propane over GaZrO x /H-SSZ-13 composite

Hydrogenation of CO2 to Light Olefins over ZnZrOx/SSZ‐13

Effective conversion of CO 2 into light olefins over a bifunctional catalyst consisting of La-modified ZnZrO x oxide and acidic zeolite

Enhancement of light olefin production in CO2 hydrogenation over In2O3-based oxide and SAPO-34 composite

ZrO2–ZnO–CeO2 integrated with nano-sized SAPO-34 zeolite for CO2 hydrogenation to light olefins

Setting up In2O3-ZrO2/SAPO-34 Catalyst for Improving Olefin Production via Hydrogenation of CO2/CO Mixtures

Indium-Promoted ZnZrO x /nano-ZSM-5 for Efficient Conversion of CO 2 to Aromatics with High Selectivity

Breaking the activity-selectivity trade-off of CO2 hydrogenation to light olefins

Role of Zr loading into In2O3 catalysts for the direct conversion of CO2/CO mixtures into light olefins

Modulation of inter-elemental synergy and oxygen vacancy content of CdZrO x solid solution catalysts by Ga for effective CO 2 hydrogenation to methanol