Na-doped Diopside Microwave Ceramics with Dielectric Properties Influenced by the Sintering, Lattice Vibration and Chemical Bond Characteristics

Fangyi Huang,Hua Su,Qin Zhang,Xiaohui Wu,Yuanxun Li,Xiaoli Tang

DOI: https://doi.org/10.1016/j.jallcom.2021.162973

IF: 6.2

2022-01-01

Journal of Alloys and Compounds

Abstract:The Na-doped diopside (CaMg1-xNa2xSi2O6, x = 0-0.18) microwave dielectric ceramics were fabricated via solid-state reaction method. Three phases were identified through the XRD data that was refined with the Rietveld method to obtain structural information. The role of Na+ substitution to promote the densification process could be corroborated by the SEM images and relative density. The P-V-L bond theory was used to explore the chemical bond characteristics and structure-performance relationships. Through discussion, the dielectric constant was determined by relative density rather than the bond ionicity. The Q x f value was dominated by the lattice energy, lattice vibration and was also related to the relative density and grain size. And the linear thermal expansion coefficient was closely correlated with the tau(f) value. Excellent microwave dielectric properties, (epsilon(r) = 7.573, Q x f = 35049 GHz, tan delta = 4.015 x 10(-4), tau(f) = -68.71 ppm/degrees C) and (epsilon(r) = 7.646, Q x f = 37844 GHz, tan delta = 3.706 x 10(-4), tau(f) = -54.2 ppm/degrees C) were achieved for the CaMg0.97Na0.06Si2O6 ceramics sintered at 1150 degrees C/3 h and 1200 degrees C/3 h, respectively. (C) 2021 Elsevier B.V. All rights reserved.