Abstract:Nano-porous metals exhibit novel physical and chemical properties, showing a promising potential for scientific research and engineering applications such as catalyst, electrochemical catalysis, detecting and sensing etc. The nano-porous materials are normally made of noble metal films by chemical dealloying about several-hundred micrometers in thickness prepared by arc melting, magnetic spattering and electrodeposit, which limits their performance and potential applications. We report a novel approach to fabricate Cu-Mn nano-porous structures on any location of conventional metallic components by laser deposition hybrid with electrolyte dealloying. Cu-Mn alloy layers with specific composition were deposited by laser onto a mild steel substrate surface. The laser deposition parameters were optimized to achieve sound Cu-Mn layers free of cracks, pores or inclusion. The deposition dilution was specifically controlled to avoid the designed composition of the Cu-Mn alloy to be modified by the melted Fe from the substrate and thus to obtain a single solid-solution microstructure, as a first precondition for forming nano-porous structure by electrolyte dealloyibng. Laser deposition offers a flexible approach to deposit designed composition with designed microstructure and geometry onto any location. The microstructure of the as-deposited layer was further processed by laser remelting for grain-size refinement to meet the second precondition. The second-dendrite-arm-spacing (SDAS) of the as-deposited structure decreases with the increase of laser remelting speed. SDAS can be decreased to 1.6μm with a laser remelting speed up to 83mm/s. Electrolyte dealloying was applied on the as-deposited and remelted layer. The polarization curves of Cu-Mn alloy were analyzed in KNO3 and HCl electrolytes to figure out their electrochemical behavior. The Cu-Mn alloy shows selective dissolution characteristics in different electrolytes. Nanoporous Cu and nanoporous Mn structures can be formed with optimal electrochemically dealloying parameters in 0.1M HCl and 0.1M KNO3 electrolytes respectively. The nano porous structure is tunable by the laser parameters and the chemical etching conditions. Nanoporous Cu structure with pore size ranging from 30 to 50nm was achieved. The nano-Mn structure displays a ribbon-like morphology with ultrahigh roughness factor up to 900. Both Cu and Mn nanostructures exhibit good performance on Surface Enhanced Raman Scattering (SERS) and superhydrophobicity. We further used laser texturing to obtain a regular micro-structure on the laser deposited CuMn surface followed by selective chemical etching to obtain a random nanoporous structure on regular microstructure-a micro/nano hierarchical structure. The regular micro-scale roughness can be tuned from 5 μm to 30 μm Rz by laser texturing while the ligament width and spacing of the random nano porosity be 10-50 nm by selective chemical etching. This unique hierarchical structure demonstrates good photocatalytic performance.

Controllable Nanoporous Copper Synthesized by Dealloying Metallic Glasses: New Insights into the Tuning Pore Structure and Applications

Fabrication of nanoporous copper with tunable ligaments and promising sonocatalytic performance by dealloying Cu–Y metallic glasses

Fabrication of Nanoporous Copper Ribbons with a Broad Range of Pore Size and Its Application in Lithium-ion Batteries

Formation of Nanoporous Copper with Hybrid-Modal Pore Size Distributions Related to Surface Diffusion of Copper Atoms During Dealloying of Mg 13.5 At.% Cu Alloy in an Acidic Solution

Formation of Monolithic Nanoporous Copper with Ultrahigh Specific Surface Area Through Chemical Dealloying of Mg-Cu Alloy

Fabrication and Degradation Properties of Nanoporous Copper with Tunable Pores by Dealloying Amorphous Ti-Cu Alloys with Minor Co Addition

A Facile One-Pot Route to Fabricate Nanoporous Copper with Controlled Hierarchical Pore Size Distributions Through Chemical Dealloying of Al–Cu Alloy in an Alkaline Solution

Influence of Alloy Composition on Nanoporous Structure by Dealloying Mn-Cu Ribbons

Fabrication and Functionalization of Tunable Nanoporous Copper Structures by Hybrid Laser Deposition and Chemical Dealloying

Nanoporous Copper from Dual-Phase Alloy Families and Its Technology Application in Lithium Ion Batteries

The Mechanical Characteristics of Monolithic Nanoporous Copper and Its Composites

Two-step Fabrication of Nanoporous Copper Films with Tunable Morphology for SERS Application

Three‐dimensional Nanoporous Copper with Tunable Structure Prepared by Dealloying Titanium–copper–cobalt Metallic Glasses for Supercapacitors

Three-dimensional Nanoporous Copper with High Surface Area by Dealloying Mg–Cu–Y Metallic Glasses

Formation and characterization of Monolithic nanoporous copper by chemical dealloying of Al-Cu alloys

Facile One-Pot Synthesis of Nanoporous Copper Ribbons with Bimodal Pore Size Distributions by Chemical Dealloying

Needle-like Cu(OH)2 in situ grown on nanoporous copper ribbon via anodizing route for supercapacitors

Dual-phase Nanostructuring As a Route to Flexible Nanoporous Metals with Outstanding Comprehensive Mechanical Properties

Bendable Nanoporous Copper Thin Films with Tunable Thickness and Pore Features

Tunable Nanoporous Metallic Structures Formed by Hybrid Laser Deposition and Chemical Etching and Their Functionalization

Nanoporous Copper Films with High Surface Area Formed by Chemical Dealloying from Electroplated CuZn Alloy