Characterization of In-Situ Reinforced (al,si)3(ti,ce) Precipitates in T6 Treated A356-0.3wt.%Ce-1.5vol.%TiCN Composite and Its Effects on Mechanical Properties

Guodong Niu,Jeff Wang,Jinping Li,Jinwen Ye,Jian Mao

DOI: https://doi.org/10.1016/j.matchar.2022.111756

IF: 4.537

2022-01-01

Materials Characterization

Abstract:In the present study, the microstructural evolution and mechanical properties of T6 treated A356-0.3wt.%Ce-1.5vol.%TiCN composite were studied. The results demonstrated that the grain refinement and eutectic Si modification effects of T6 treated A356-0.3wt.%Ce-1.5vol.%TiCN composite are remarkable than that of T6 treated A356 alloy, and similar to that of T6 treated A356-0.3wt.%Ce alloy. More importantly, the in-situ reinforced (Al,Si)(3)(Ti,Ce) precipitates were found in T6 treated A356-0.3wt.%Ce-1.5vol.%TiCN composite. TEM results and simulated diffraction pattern corresponding to the proposed crystal structure indicated that the (Al,Si)(3)(Ti,Ce) precipitates could be indexed consistently according to a body-centered tetragonal structure (14/mmm space group, D022 type) with lattice parameters approximately of a = 0.519 nm and c = 0.859 nm. The existence of (Al,Si)(3)(Ti,Ce) precipitates resulted in the increase of strength due to the load bearing and coefficient of thermal expansion (CTE) mismatch strengthening. Besides, the fracture mode of the T6 treated A356-0.3wt.% Ce-1.5vol.%TiCN composite is a transgranular fracture. Compared with the T6 treated A356-0.3wt.%Ce alloys, A356-0.3wt.%Ce-1.5vol.%TiCN alloys showed better elongation, which is ascribed to the transformation of needle-like and hard Ce-rich phases distributing along with the eutectic Si to blocky and relatively soft (Al, Si)(3)(Ti,Ce) phases. The ultimate tensile strength (TITS) and the elongation (El) of the A356-0.3wt.%Ce-1.5vol.% TiCN composite were increased by 3.7% and 32.7% than that of the A356-0.3wt.%Ce alloy, respectively.