Abstract:Sulfur oxides present in flue gas can deactivate metal oxide catalysts or metal cation exchange zeolite catalysts used in NH 3 -SCR, as the deposition of (NH 4 ) 2 SO 4 /NH 4 HSO 4 and metal sulfate can obstruct and damage active sites, respectively. The physical poisoning of the (NH 4 ) 2 SO 4 /NH 4 HSO 4 deposition can be prevented by selecting an appropriate reaction temperature range (reversible), while chemical poisoning caused by the sulfation of active sites is challenging to avoid and can permanently deactivate the catalyst (irreversible). This research addresses the issue of irreversible catalyst deactivation resulting from sulfur poisoning by employing metal-free β zeolite without redox sites, which effectively prevents redox site sulfation at its source and shields the catalyst from physical poisoning by operating at moderate to high temperatures. This metal-free β zeolite with an appropriate pore structure exhibited exceptional deNO x activity, N 2 selectivity, stability, and sulfur resistance at 300 °C. The NO oxidation experiment and DFT analysis demonstrated that the specific pore structure of β zeolite functioned as a sub-nano reactor, facilitating the oxidation of NO to NO 2 , thereby triggering the subsequent series catalytic reaction of "fast" SCR. Even in an atmosphere with a high concentration of 300 ppm SO 2 , the β zeolite catalyst maintained over 80 % NO x conversion after 130 h. The slight reduction in activity was attributable to the inhibitory influence of SO 2 on the collision reaction between NO and O 2 ; however, SO 2 did not have any poisonous impact on the catalyst. The unique design strategy found in present work provides valuable insights for the sulfur resistance of metal-free zeolites used in NH 3 -SCR process, and provides a new idea for the design of completely sulfur-resistant catalysts.

Active centers response to SO<sub>2</sub> and H<sub>2</sub>O poisoning over Fe-W-Ni exchanged zeolite for high-temperature NH<sub>3</sub>-SCR: Experimental and DFT studies

Unraveling Alkali-Tolerance Role of Zeolite Coupling CeWOx Catalyst for NOx Reduction

Experimental and Density Functional Theory Studies on the Zeolite-Based Fe–Ni–W Trimetallic Catalyst for High-Temperature NOx Selective Catalytic Reduction: Identification of Active Sites Suppressing Ammonia Over-oxidation

Insight into the SO2 poisoning of heterobimetallic FeCu‐SSZ‐13 zeolite in NH3‐SCR reaction

Discovering the Remarkable Denox Activity and Anti-K Poisoning of MnFeOx/H-Beta Composite Catalyst

Cu-SSZ-13 zeolite–metal oxide hybrid catalysts with enhanced SO2-tolerance in the NH3-SCR of NOx

Selective Catalytic Reduction of NOx with NH3 over Short-Range Ordered W-O-Fe Structures with High Thermal Stability

Metal-free β zeolite used as an efficient NH 3 -SCR catalyst can achieve complete immunity to SO 2 : Unique design strategy of sulfur-resistant catalyst

Unraveling alkali-tolerance role of zeolite coupling CeWOx catalyst for NO reduction

Alkali poisoning of Fe-Cu-ZSM-5 catalyst for the selective catalytic reduction of NO with NH3

Accelerator or Inhibitor? The Effects of H 2 O on Selective Catalytic Reduction of NO x by Methanol over HZSM-5 Catalysts with Different Lewis/Brønsted Ratios

Highly Dispersed Iron Species Created on Alkali-Treated Zeolite for Ammonia SCR

Widened Active Temperature Window of a Fe-ZSM-5 Catalyst by an Impregnation Solvent for NH3-SCR of NO

Alkali Metal Poisoning of A Ceo2-Wo3 Catalyst Used in the Selective Catalytic Reduction of Nox with Nh3: an Experimental and Theoretical Study

In situ DRIFTS and DFT studies of SO2 poisoning over Cu-exchanged X zeolite catalyst for NH3-SCR

Mechanistic investigation of Sm doping effects on SO2 resistance of W-Zr-ZSM-5 catalyst for NH3-SCR

Insight into the SO<sub>2</sub> resistance mechanism on -Fe<sub>2</sub>O<sub>3</sub> catalyst in NH<sub>3</sub>-SCR reaction: A collaborated experimental and DFT study

Unlocking Mixed-Metal Oxides Active Centers via Acidity Regulation for K&SO 2 Poisoning Resistance: Self-Detoxification Mechanism of Zeolite-Confined de NO x Catalysts

Acidified SiO2 Supported Fe-based Bimetal Oxide Catalyst with Resistance to High-Level Alkali Poisoning for CO Selective Catalytic Reduction of NO Removal of NOx

Evolution Mechanism of NOx in NH3-SCR Reaction over Fe-ZSM-5 Catalyst: Species-performance Relationships

Innovative In/H-SSZ-39 Catalysts: An Exploration in NOx Reduction via CH4-SCR