Composition engineering of lead-free double perovskites towards efficient warm white light emission for health and well-being

Peifen Zhu,Saroj Thapa,Hongyang Zhu,Stephen Wheat,Yang Yue,Dilip Venugopal

DOI: https://doi.org/10.1016/j.jallcom.2023.170836

IF: 6.2

2023-06-09

Journal of Alloys and Compounds

Abstract:Lead-free halide double perovskites (DPs) [A 2 B(I)B(III)X 6 ] (A: monovalent cation, B(I): monovalent cation, B(II): trivalent cation, X: halide anion) has drawn tremendous attention because of their environmental-friendliness and high stability compared to traditional lead-based perovskites ABX 3 (A: monovalent cation; B: Pb 2+ ; X: halide anion). The optoelectronic properties of DPs are, however, compromised. This work provides a methodology for improving the photophysical properties of DPs and achieving high-efficiency warm white light emission. First principles density functional theory (DFT) was used in material design and the ligand-free synthesis of halide DP Cs 2 Ag 1−x K x In 0.875 Bi 0.125 Cl 6 (x ≤ 0.60) via a facile recrystallization process was demonstrated. The compositional tuning of K + to Ag + resulted in an improvement in photophysical properties. Independent of K + content, all the samples exhibit strong absorption at a wavelength of λ max ∼ 375 nm with a direct bandgap which is consistent with our DFT calculation results. Broadband photoluminescence (PL) emission profiles covering the spectra from blue to deep red (405–820 nm at λ max ∼ 629 nm) were observed. Besides, with an optimized K + alloying content of 0.20, the optical performance of these halide DPs was impressively regulated, demonstrating improved photoluminescence quantum yield (PLQY) of host Cs 2 AgInCl 6 crystals from ∼ 2.70 % (x = 0) to ∼15.96 % (x = 0.20), due to increased radiative recombination of self-trapped excitons. the highest report for such structures. It also shows high stability over 180 days. Furthermore, the use of blue-emitting CsPbBr 3 and DP Cs 2 Ag 0.80 K 0.20 In 0.875 Bi 0.125 Cl 6 as color conversion layers in white light-emitting diodes (LEDs) demonstrates that high-quality white light emission with the CIE color coordinate of (0.387, 0.385) and a correlated color temperature (CCT) of 3878 K, color rendering index (CRI) of 85, and luminous efficacy of radiation (LER) of 214 lm/W. Hence, the research work provides insight into realizing environmentally friendly and high-efficiency white light emission with high color quality by using earth-abundant elements and the low-cost synthesis method.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering