Facile Melting-Crystallization Synthesis of Cs 2 Na x Ag 1– x InCl 6 : Bi Double Perovskites for White Light-Emitting Diodes

Xiaoxi Li,Weiwei Li,Mengling Xia,Chao Liu,Neng Li,Zuhao Shi,Yinsheng Xu,Xianghua Zhang

DOI: https://doi.org/10.1021/acs.inorgchem.1c03996

IF: 4.6

2022-03-11

Inorganic Chemistry

Abstract:Lead-free double perovskites (DPs) have outstanding luminescent properties, which make them excellent candidates for wide use in optoelectronics. Herein, a solvent-free melting-crystallization technique, which can produce kilogram-scale DP microcrystals (DP-MCs) in one batch, is invented to synthesize the Cs2NaxAg1–xInCl6: Bi (x = 0, 0.2, 0.4, 0.6, 0.8, and 1) DP-MCs. The structure and composition analysis confirmed the products are pure Cs2NaxAg1–xInCl6 DP-MCs. Affected by Jahn–Teller distortion of AgCl6 octahedra, self-trapped excitons appear in the excited state, resulting in the broadband emission (400–850 nm) of Cs2Ag1–xNaxInCl6: Bi DP-MCs. The enhancement of the photoluminescence quantum yield can be realized by introducing Na+ to break the parity-forbidden transition in the Cs2AgInCl6 DP. Optimized Cs2Na0.4Ag0.6InCl6: Bi DP-MC phosphors combined with commercial blue and green phosphors were coated on ultraviolet chips (365 nm) to fabricate white light-emitting diodes (WLEDs) from warm white (2930 K) to cold white (6957 K). An ultrahigh color rendering index of 97.1 and a CCT of 5548 K as well as Commission Internationale de l'Eclairage color coordinates of (0.331, 0.339) have been demonstrated. This kilogram-scale synthesis technique could stimulate the industrial development of WLEDs for general lighting based on DP-MC phosphors.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.inorgchem.1c03996.Differential thermal analysis (DTA) and thermogravimetric analysis (TGA) data (Figure S1), calculated formation energy data (Table S1), SEM images and EDS data (Figures S2 and S3 and Table S2), Raman spectra (Figure S4), and optical properties (Figures S5–S9 and Tables S3 and S4) (PDF)This article has not yet been cited by other publications.

chemistry, inorganic & nuclear