Flame Retardancy and Mechanical Properties of Chitosan and DOPO with Different Mass Ratios in Epoxy Resin

Junjie Wang,Xinyu Wang,Chenyu Zhou,Zhiquan Pan,Hong Zhou

DOI: https://doi.org/10.21203/rs.3.rs-1095633/v1

2021-01-01

Abstract:This work focused on the effects of chitosan (CS) and 9,10-dihydro-9-oxo-10-phosphaphenanthrene-10-oxide (DOPO) on the flammable propertied of epoxy resin matrix. The EP composites were fabricated by direct mixing method through a general curing method. The influence of CS, DOPO and CS / DOPO on the resin was investigated through cone calorimetry tests (CC), UL-94 vertical burning, limiting oxygen index (LOI), thermal gravimetric analyzer (TGA), differential scanning calorimeter (DSC) and thermogravimetric analyzer-Fourier infrared combined system (TG-FTIR). The char residues of modified EPs after CC tests were investigated by FTIR, EDX and XPS. Under the 10% addition of CS / DOPO in EP, with the mass ratio of CS and DOPO of 1 : 1, 1 : 2, 1 : 3, 2 : 1 and 3 : 1, the flame retardancy properties of EPs all increased, but only if EP/10% CS1/DOPO2 and EP/10% CS2/DOPO1 achieved a V-0 rating and their values of LOI were 33.7% and 32.5%, respectively. Compared with EP, the peak heat release rate, peak smoke produce rate and total heat release of EP/10% CS1/DOPO2 and EP/10% CS2/DOPO1 decreased, especially, total smoke release decreased by 61.9% and 71.0%, the char residuals amount increased by 84.3% and 41.6%, and the average CO2 yield decreased by 55.4% and 55.0%, respectively. It is worth nothing that the mechanical properties increased, especially the flexural strength increased by 36.0% and 38.4%, respectively. The results indicated that DOPO and CS had important synergistic effects for simultaneous increase both the flame retardancy and mechanical properties of EP composites.