Abstract:Pt electrocatalyst durability in polymer electrolyte fuel cells (PEFCs) is generally evaluated through an accelerated stress test (AST); for example, one AST features repeated square-wave cycling with H 2 /N 2 between 0.6 V to 0.95 V vs. reversible hydrogen electrode (RHE) [1]. A separate triangular-wave AST with a higher potential range (1 – 1.5 V vs. RHE) assesses the durability of carbon-based supports [2]. Recent studies [3]–[5] have revealed the heterogeneous nature of cathode catalyst layer degradation. In general, Pt particle size growth mimics the flow field geometry with greater particle size growth under lands compared to channels. Additionally, growth is typically shown to be greater near the air outlet than the inlet and is assumed to be correlated to local performance decay. The impact of such localized degradation on distributed cell performance is investigated in this work. In the present study, a segmented cell is used to quantify functional dependence of local current distributions in aged samples to heterogeneous catalyst layer degradation (Pt particle size growth and carbon support corrosion). The outcome of this enhanced understanding is to identify limiting factors in cell performance at end-of-life (EOL). Single cell studies with 25-cm 2 active area are performed using catalyst-coated Nafion ® XL membranes (Ion Power Inc.) and SGL-22 BB gas diffusion layers (GDLs) as membrane electrode assembly (MEA) materials and 7-channel serpentine flow field. An S++ ® current scan shunt (CSS) sensor plate (25-cm 2 ) with 100 current and 25 temperature measurement segments is utilized for current and temperature mapping, respectively. The MEAs are subjected to DOE's square-wave cycling (0.6 to 0.95 V vs. RHE), triangular-wave cycling (1 to 1.5 V vs. RHE), and a sequence of square-wave cycling followed by triangular-wave cycling. Complete in-situ electrochemical characterization and post-mortem ex-situ diagnostics such as micro-X-ray diffraction (micro-XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) are used to obtain particle size distribution and spatial degradation profiles. Results indicate a strong dependence of current distributions on localized catalyst layer degradation. For example, MEA with relatively uniform current distributions at the beginning-of-life (BOL) in Figure 1 exhibits severe mass transport limitations (significantly higher current at the air inlet than the outlet) at EOL when subjected to triangular-wave carbon corrosion AST. Furthermore, an increase of ~1.5x in Tafel slope is observed for the aged sample at EOL, highlighting increased transport losses. These mass transport losses are believed to originate from loss of catalyst layer porosity and subsequent compaction due to carbon support corrosion [2]. This work seeks to achieve a greater understanding of the functional dependence between catalyst growth and carbon corrosion and observed local performance. References: [1] S. Stariha et al., "Recent Advances in Catalyst Accelerated Stress Tests for Polymer Electrolyte Membrane Fuel Cells," J. Electrochem. Soc., vol. 165, no. 7, pp. F492–F501, 2018, doi: 10.1149/2.0881807jes. [2] N. Macauley et al., "Carbon Corrosion in PEM Fuel Cells and the Development of Accelerated Stress Tests," J. Electrochem. Soc., vol. 165, no. 6, pp. F3148–F3160, 2018, doi: 10.1149/2.0061806jes. [3] L. Cheng et al., "Mapping of Heterogeneous Catalyst Degradation in Polymer Electrolyte Fuel Cells," Adv. Energy Mater., vol. 2000623, pp. 1–7, 2020, doi: 10.1002/aenm.202000623. [4] P. Sharma et al., "Influence of Flow Rate on Catalyst Layer Degradation in Polymer Electrolyte Fuel Cells," {ECS} Meet. Abstr., vol. {MA}2020-0, no. 36, p. 2345, Nov. 2020, doi: 10.1149/ma2020-02362345mtgabs. [5] K. Khedekar et al., "Probing Heterogeneous Degradation of Catalyst in PEM Fuel Cells under Realistic Automotive Conditions with Multi-Modal Techniques," Adv. Energy Mater., 2021, doi: 10.1002/aenm.202101794. Figure 1

Comparison of the performance and degradation mechanism of PEMFC with Pt/C and Pt black catalyst

Performance degradation of 1 kW proton exchange membrane fuel cell stack using graphitized carbon supported Pt nanoparticle catalyst

Quantification and evolution on degradation mechanisms of proton exchange membrane fuel cell catalyst layer under dynamic testing conditions

Comparative Investigation on the Activity Degradation Mechanism of Pt/C and PtCo/C Electrocatalysts in PEMFCs during the Accelerate Degradation Process Characterized by an in Situ X-ray Absorption Fine Structure

A perspective on influences of cathode material degradation on oxygen transport resistance in low Pt PEMFC

Degradation Investigation of Electrocatalyst in Proton Exchange Membrane Fuel Cell at a High Energy Efficiency

Understanding the Degradation of Pt Electrocatalysts in Proton Exchange Membrane Fuel Cells by 3D Identical Location STEM

Understanding the Degradation Mechanisms of Pt Electrocatalysts in PEMFCs by Combining 2D and 3D Identical Location TEM

Investigation of Catalyst Degradation in Proton Exchange Membrane Fuel Cell By Identical Location Electron Microscopy

Mitigation of Performance Degradation of Cathodes for Polymer Electrolyte Membrane Fuel Cells

Investigations in High-Efficiency PGM-Catalyst MEA and Its Long-Period Degradation Mechanism for PEMFC in Heavy-Duty Vehicles

Research progress of PEMFC degradation in full operating modes for electric vehicle

Operando deconvolution of the degradation mechanisms of iron–nitrogen–carbon catalysts in proton exchange membrane fuel cells

Insight into the Rapid Degradation Behavior of Nonprecious Metal Fe-N-C Electrocatalyst-Based Proton Exchange Membrane Fuel Cells

Performance degradation and process engineering of the 10 kW proton exchange membrane fuel cell stack

Impact of Pt-Loading and Carbon Support of Pt/C Anode Catalysts on Membrane Degradation Rate in Fuel Cells

Localized Electrochemical Performance Degradation in Polymer Electrolyte Fuel Cells (PEFCs)

Catalyst Degradation Mitigation and Fuel Utilization Enhancement of a Dead-Ended Anode and Cathode Proton Exchange Membrane Fuel Cell with Periodical Oxygen Supply

Post mortem Study of Catalyst Degradations Occurring in High-Temperature Proton Exchange Membrane Fuel Cells Upon Start-Stop Operation

Effect of load-cycling amplitude on performance degradation for proton exchange membrane fuel cell

Degradation Characteristics of Membrane Electrode Assembly under Drive Cycle Test Protocol