Abstract:Failure mechanisms of thermal barrier coating system (TBCs) are complicated, wherein spalling of ceramic top coat (TC) caused by the interfacial oxidation is the most important factor. The present paper focuses on clarifying the impact of continuous formation of thermally grown oxide (TGO) on the shielding/anti-shielding and deflection of surface cracks within the TC. The growth stress in the TC due to the expansion of TGO layer is taken into account by introducing a new three-layered model in TBCs where the initial residual stress in TC is also presented. The theory of material configurational force is innovatively used to analyze the influence of the growth of TGO layer on the crack-tip driving force, i.e., the J(k)-integral. A fracture criterion is employed to predict the deflection of lengthways propagation of the surface crack via the maximum energy release rate associated with J(k)-integral. The influences of the key factors such as the initial crack length, the initial crack inclination angle, the magnitude of growth eigenstrain of TGO, the dwelling time of TGO at elevated temperature on the propagation of surface cracks are analyzed. Numerical results verify that the growth of TGO layer significantly impacts the failure of TBCs, particularly the lateral growth behavior of TGO layer is the key factor influencing the initiation and propagation of surface crack at elevated temperature. The lateral expansion growth of TGO layer induced additional tensile stress in TC can accelerate the initiation of surface cracks. Furthermore, the TGO growth can partly suppress/enhance the deflection of surface crack depending on the inclination angle and the suppression/enhancement effect becomes stronger as the dwelling (oxidation) time increases. (C) 2016 Elsevier B.V. All rights reserved.

Critical Scale Grain Size for Optimal Lifetime of TBCs

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Comprehensive Dynamic Failure Mechanism of Thermal Barrier Coatings Based on a Novel Crack Propagation and TGO Growth Coupling Model

Thermomechanical and Thermal Gradient Mechanical Fatigue Lifetime of Thermal Barrier Coating Systems

Effect of TGO Thickness on Thermal Cyclic Lifetime and Failure Mode of Plasma‐Sprayed TBCs

Comprehensive Effects of TGO Growth on the Stress Characteristic and Delamination Mechanism in Lamellar Structured Thermal Barrier Coatings

The Impact of the Growth of Thermally Grown Oxide Layer on the Propagation of Surface Cracks Within Thermal Barrier Coatings

Thermal cycling induced crack nucleation and propagation in thermal barrier coating system

Influence of Composition of TGO on the Thermal Shock Lifetime of Thermal Barrier Coatings with Cold-Sprayed MCrAlTaY Bond Coat

The Combined Effect of Creep and TGO Growth on the Cracking Driving Force in a Plasma-Sprayed Thermal Barrier System

Effect of Thermal Growth Oxide Composition and Morphology on Local Stresses in Thermal Barrier Coatings

Dynamic Crack Growth Mechanism and Lifetime Assessment in Plasma Sprayed Thermal Barrier System Upon Temperature Cycling

An Innovative Model Coupling TGO Growth and Crack Propagation for the Failure Assessment of Lamellar Structured Thermal Barrier Coatings

Microstructure characteristics and deformation-induced crystalline-to-amorphous phase transformation in thermal barrier coatings during thermal cycling

Effect of TGO on the Tensile Failure Behavior of Thermal Barrier Coatings

Dynamic Multi-Crack Evolution and Coupling TBC Failure Together Induced by Continuous TGO Growth and Ceramic Sintering

Comprehensive Understanding of the Effect of TGO Growth Modes on Thermal Barrier Coating Failure Based on a Simulation

Stress States and Crack Behavior in Plasma Sprayed TBCs Based on a Novel Lamellar Structure Model with Real Interface Morphology

Failure Behaviors of EB-PVD Thermal Barrier Coatings under Isothermal Oxidation and Thermal Cycling Conditions

Sintering Induced the Failure Behavior of Dense Vertically Crack and Lamellar Structured TBCs with Equivalent Thermal Insulation Performance

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient