Optical properties and nanosecond laser damage characterization of liquid crystal polarization gratings
Kun Yu,Zhouhao Zhang,Yuanan Zhao,Jianguo Wang,Wenbin Huang,Zhichang Mo,Yi Chen,Kun Wang,Xiaofeng Liu,Zhaoliang Cao,Jianda Shao
DOI: https://doi.org/10.1016/j.optmat.2023.114755
IF: 3.754
2023-12-24
Optical Materials
Abstract:Liquid crystal polarization gratings (LCPGs) possess unique optical properties and therefore are widely used in laser systems. Therefore, developing our understanding of the laser damage resistance of LCPGs is critical for future high-intensity laser applications. In this study, the LCPGs ( Λ = 8 μm) were fabricated from liquid crystal polymer (LCP) films with photo-alignment technology, which had a small-angle (∼7.51°) diffraction order with high diffraction efficiency (∼92 %) under chiral polarized incidence at 1064 nm. The diffraction efficiency and polarization of each diffraction order were determined by the polarization of the incident light. The damage characteristics of the LCPGs were investigated using a chiral polarized nanosecond laser at 1064 nm in a one-on-one test. The laser-induced damage thresholds (LIDTs) of left-handed circular polarization (LHCP) and right-handed circular polarization (RHCP) were 8.0 J/cm 2 and 8.5 J/cm 2 , respectively. For comparison, the LIDTs of S-polarization and P-polarization were 7.8 J/cm 2 and 8.4 J/cm 2 , respectively. All the damage occurred at the interface between the LCP layer and the substrate when the laser fluence was near the LIDT, and the damage morphology was observed with a scanning electron microscope (SEM), including flat pits, cracks, and bumps at the edge of the pits. The results indicate that the LIDTs and damage morphology of the LCPGs were insensitive to the polarization of the irradiation. The electrical effects of differently polarized irradiation on the LCPGs were simulated using the finite element method (FEM). The electric field distribution was symmetrical under irradiation by LHCP and RHCP lasers. However, the distribution of the electric field under different linearly polarized irradiation conditions were distinct. Based on these findings, we believe that the contribution of chiral polarized irradiation to the damage was consistent and that the LIDTs were similar. This study has important implications for the application and development of LCPGs in high-intensity laser systems.
materials science, multidisciplinary,optics