Abstract:A coordination-assisted pyrolysis procedure was adopted to encapsulate palladium (Pd) nanoparticles in a mesoporous carbonaceous matrix. X-ray diffraction and transmission electron microscopy measurements revealed that approximately 2.5 nm nanoparticles were highly dispersed inside the well-ordered porous framework. High-resolution TEM and temperature-programmed hydride decomposition analysis demonstrated the formation of interstitial carbon in the Pd lattice. Diffuse reflectance infrared Fourier transform spectroscopy indicated that carbon species could be deposited on low-coordinated surface sites of the Pd particles. This catalyst exhibited high activity in the selective hydrogenation of cinnamaldehyde (CAL) at 80 degrees C under an H-2 pressure of 1.0 MPa (turnover frequency (TOF) of 2.4 s(-1)) to produce hydrocinnamyl aldehyde with high selectivity (HCAL; approximately 80%) in water and could be reused eight times with no dear activity loss. A trapping agent poisoning experiment using solid SH-SBA-15 revealed unobvious leaching of Pd into the solution. Exposure to thiourea with a S:Pd ratio of 0.1 resulted in slight activity and undetectable selectivity losses over the current catalyst in the selective hydrogenation of CAL at 80 degrees C under an H2 pressure of 1.0 MPa. However, a 50% activity loss was observed for commercial Pd/C. Even after an increase in the thiourea concentration to a S:Pd ratio of 3, the TOF remained at 1.9 s(-1) with a negligible effect on the HCAL selectivity. Nearly complete deactivation of Pd/C occurred upon high exposure to thiourea. DFT calculations showed that the presence of surface or subsurface carbon can enhance the poison tolerance of the encapsulated Pd catalysts. The enhanced hydrogenation activity and strong poison tolerance are consistent with the interpretation that Pd nanoparticles are modified by carbonaceous deposits.

Honeycomb-like Nitrogen-Doped Porous Carbon Nanosphere Encapsulated Ultrafine Pd Nanoparticles for Selectively Catalyzing Hydrogenation of Cinnamaldehyde in Water

Nickel Nanoparticles Embedded in Porous Carbon-Coated Honeycomb Ceramics: A Potential Monolithic Catalyst for Continuous Hydrogenation Reaction

Sulfur-doped Porous Carbon Supported Palladium Catalyst for High Selective O-Chloro-nitrobenzene Hydrogenation

Hexagonal Boron Nitride Sheet-Anchored Palladium‑nickel Nanoparticles for Highly Selective Hydrogenation of Cinnamaldehyde under Mild Conditions

Hydrophobic and Porous Fe-Pdb Coordination Framework Structure Supported Pt-Fe Nanoparticles Catalyst for Enhanced Chemoselective Hydrogenation of Cinnamaldehyde

Room-Temperature Tandem Condensation-Hydrogenation Catalyzed by Porous C3N4 Nanosheet-Supported Pd Nanoparticles

Carbon Nanotubes Supported Palladium Catalysts for Selective Hydrogenation of Cinnamaldehyde under Atmospheric Pressure

Poison Tolerance to the Selective Hydrogenation of Cinnamaldehyde in Water over an Ordered Mesoporous Carbonaceous Composite Supported Pd Catalyst

Tunable Selective Hydrogenation of Cinnamaldehyde by Capped Pt/Pd Nanoparticles Supported on Carbon Nanotubes

Ultrafine Palladium Nanoparticles Deposited on Ni, N Co-Doped Carbon to Boost Dehydrogenation Efficiency of Perhydro-N-Phenylcarbazole

Pd-Decorated Hierarchically Porous Carbon Nanofibers for Enhanced Selective Hydrogenation of Phenol

Space-Confined Carbon-Doped Pd Nanoparticles as a Highly Efficient Catalyst for Selective Phenol Hydrogenation

Single Palladium Atoms Stabilized by Β-Feooh Nanorod with Superior Performance for Selective Hydrogenation of Cinnamaldehyde

Dendrimer-Encapsulated Pd Nanoparticles, Immobilized in Silica Pores, as Catalysts for Selective Hydrogenation of Unsaturated Compounds

Utilizing in situ construction of N-doped hierarchical porous carbon to achieve electronic control of highly dispersed Pd nanoparticles for efficient catalytic hydrogenation of CO 2 to formic acid

NiPt Nanoparticles Anchored Onto Hierarchical Nanoporous N-Doped Carbon As an Efficient Catalyst for Hydrogen Generation from Hydrazine Monohydrate.

Easily Recyclable Pd-Decorated Hierarchically Porous Nanofibers for the Selective Hydrogenation of Phenol

Three-dimensional hydrophobic porous organic polymers confined Pd nanoclusters for phase-transfer catalytic hydrogenation of nitroarenes in water

Magnetic Anchored CoPt Bimetallic Nanoparticles As Selective Hydrogenation Catalyst for Cinnamaldehyde

CO2‐assisted Controllable Synthesis of PdNi Nanoalloys for Highly Selective Hydrogenation of Biomass‐derived 5‐Hydroxymethylfurfural

Pd cluster nanowires as highly efficient catalysts for selective hydrogenation reactions.