In-situ TEM investigation of 30 keV he+ irradiated tungsten: Effects of temperature, fluence, and sample thickness on dislocation loop evolution
Yipeng Li,Li Wang,Guang Ran,Yue Yuan,Lu Wu,Xinyi Liu,Xi Qiu,Zhipeng Sun,Yifan Ding,Qing Han,Xiaoyong Wu,Huiqiu Deng,Xiuyin Huang
DOI: https://doi.org/10.1016/j.actamat.2020.116618
IF: 9.4
2021-03-01
Acta Materialia
Abstract:<p>In-situ irradiations with 30 keV He<sup>+</sup> were performed on tungsten in an investigation of the influences of irradiation temperature and fluence, pre-existing dislocation and sample thickness on dislocation loop evolution including interaction, density and size. Dislocation loops with <strong><em>b</em></strong> = 1/2<111> and <strong><em>b</em></strong> =<100> were found to form in tungsten during irradiation. The ratio of <100> loops was obviously affected by irradiation temperature, fluence, sample thickness and pre-existing dislocation lines. The interaction between high density helium clusters could stimulate the formation of <100> loops in irradiated W, which was verified by Molecular Dynamic (MD) simulations. In addition, the driving force for the <100> loop formation should also be attributed to the reaction of two 1/2<111> loop variants driven by long-time and elevated temperature irradiation. The pre-existing dislocation lines were found to have a profound effect on the size, density and Burgers vector of dislocation loops. Additionally, irradiation-induced defects were likely to be absorbed by the surface sinks of thin foil during ion irradiation, resulting in the formation of a denuded zone near the surface. The in-situ observation of irradiation defect evolution will lead to an improved fundamental understanding of irradiation damage process of tungsten serviced in fusion reactor.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering