Abstract:The polycrystalline IN713C produced via investment casting is one of the widely-used nickel-based superalloy in automotive and aerospace industries. This alloy, however, has an apparent inhomogeneous microstructure generated during casting and contains dendritic structure that gives rise to strain localisation during loading. Yet, the effect of dendrite structure, grain size and shape as well as crystallographic orientation, which directly influence fatigue property and deformation micromechanism in the components, is rarely studied. In the present study, IN713C cast bars are tailored with three different grain structures, i.e., transition, equiaxed and columnar, with substantial grain size variations. The produced bars were tested under strain controlled LCF (Low Cycle Fatigue) and stress controlled HCF (High Cycle Fatigue) conditions at 650 °C. The results showed that most of fatigue cracks initiated from casting porosities and fatigue life extended in the microstructure with a small grain size during both HCF and LCF loadings. It is also demonstrated that fatigue striations were mainly observed within dendrite areas during crack propagation, whereas the higher GND (Geometrically Necessary Dislocation) density were predominantly observed in the interdendrite areas. Here, we propose a concept of 'Crack Propagation Unit (CPU)' for better description of deformation mechanism at local scale during fatigue loading by combining fracture surface characteristic methodology and dislocation distribution analyses within the dendrite structural unit. Furthermore, this model to understand the deformation micromechanism can provide a new perspective on the interpretation of Hall-Petch relationship in casting materials that contain dendritic structure. This is further demonstrated via direct correlation of the high crack propagation resistance with the crack path divergence instead of the dislocation pile-up at the grain boundary or in-between the γ/ γ' channels. Moreover, by utilising serial sectioning method followed by layered EBSD scanning, quasi-3-D grain orientation mappings were obtained, and crystallographic texture information were directly correlated with the fracture surface observations. This allowed an investigation of the influence of orientation of individual grains and micro/macro texture on crack propagation rate. The critical stage of crack propagation in fatigue life and its correlations with microstructural features is established, offering potential practical applications by controlling the investment casting process parameters.

Modeling of the Fatigue Crack Growth of Nickel-Based Superalloy Using a Constraint-Based Approach Considering Thickness

Influence of orientation and temperature on the fatigue crack growth of a nickel-based directionally solidified superalloy

A combined cyclic viscoplasticity and entropy generation approach for modelling fatigue crack growth behavior of nickel-based superalloy at high temperature

Micro-notch Size Effect on Small Fatigue Crack Propagation of Nickel-Based Superalloy GH4169

A High Temperature Fatigue Damage Model for Single Crystal Superalloys

Fatigue Life Prediction of Film-cooling Hole Specimens with Initial Damage

Low Cycle Fatigue Lifetime and Deformation Behaviour Prediction of Nickel-Based Single Crystal Superalloy Considering Thickness Debit Effect

Fatigue and Fracture Behaviors of Nickel-Based Forging Gh4169 Superalloy and Optimization of Model Parameters

A Concise Binomial Model for Nonlinear Creep-Fatigue Crack Growth Behavior at Elevated Temperatures

Fatigue Life Prediction of Nickel-Based GH4169 Alloy on the Basis of a Multi-Scale Crack Propagation Approach

A modified damage-coupled viscoplastic constitutive model for capturing the asymmetric behavior of a nickel-based superalloy under wide creep-fatigue loadings

Effect of sustained load on fatigue crack growth behavior of FGH96 at elevated temperature

Grain Size Effect on the Small Fatigue Crack Initiation and Growth Mechanisms of Nickel-Based Superalloy GH4169

Low-cycle Fatigue Life Prediction of a Polycrystalline Nickel-Base Superalloy Using Crystal Plasticity Modelling Approach

Fatigue Life Estimation of Nickel-Based Single Crystal Superalloy with Different Inclined Film Cooling Holes: Initial Damage Quantification and Coupling of Damage-Fracture Mechanics Models

Fatigue Notch Strengthening Effect of Nickel-based Single Crystal Superalloys under Different Stress Ratios

Evaluation of the Influences of the Stress Ratio, Temperatures, and Local Microstructure on Small Fatigue Crack Propagation Behavior of the FGH96 Superalloy

Thermodynamic Entropy-Based Fatigue Life Assessment Method for Nickel-Based Superalloy GH4169 at Elevated Temperature Considering Cyclic Viscoplasticity

Fatigue Behavior and Life Prediction Model of A Nickel-Base Superalloy under Different Strain Conditions

Microstructural size effect on the notch fatigue behavior of a Ni-based superalloy using crystal plasticity modelling approach

The Effects of Grain Size, Dendritic Structure and Crystallographic Orientation on Fatigue Crack Propagation in IN713C Nickel-Based Superalloy