Transition metal nitride coated with atomic layers of Pt as low-cost and high-stable electrocatalysts for oxygen reduction reac

Xinlong Tian,Junming Luo,Haobing Zou,Rong Chen,Ting Shu,Xiuhua Li,Yingwei Li,Huiyu Song,Shijun Liao,Dong Su,Radoslav R. Adzic

2016-01-01

Abstract:The high cost caused mainly by the usage of precious Pt to against sluggish kinetics of the oxygen reduction reaction (ORR) at the cathode, catalyst degradation and carbon-support corrosion are three of the most challenges for the commercial viability of polymer electrolyte membrane fuel cells (PEMFCs). To address these obstacles, we aimed towards carbon-free and robust transition metal nitride (TMN) with low Pt content materials exhibited tunable physical and catalytic properties. Here, we report a high performance low Pt catalyst prepared by covering Pt atoms on the nanoparticles of titanium nickel binary nitride (TiNiN) with several atomic layers. Towards the oxygen reduction reaction (ORR), the novel catalyst exhibited over 400% increase in mass activity and over 200% increase in specific activity when compared with the commercial Pt/C catalyst. The catalyst also showed excellent stability/durability, after 10, 000 potential cycles, only a slight performance loss could be observed, meanwhile, the structure of the catalyst was perfectly maintained, as established by TEM results. The outstanding performance of the catalyst may be resulted from the ultra high dispersion of Pt (several atoms layer coated on the nitride nanoparticles), and the excellent stability/durability may arise from the good stability of nitride, and the synergetic effects between ultra thin Pt layer and the robust TMN support. Actually, no Pt diffraction can be detected by XRD analysis and no Pt nanoparticles can be observed by TEM measurements for Pt coated nitrides, but Pt can be detected by the XPS, and its thin layer can be observed by the HRTEM on the surface of nitride nanopartilces, confirming the high dispersion of Pt on the surface of nitride nanoparticles. Further, the significant shift of Pt 3d binding energy evidences the interaction between Pt and nitrides.