Microstructure and properties of Cu–Ni–Co–Si–Cr–Mg alloys with different Si contents after multi-step thermo-mechanical treatment
Muzhi Ma,Zhou Li,Zhu Xiao,Yanlin Jia,Xiangpeng Meng,Yanbin Jiang,Yue Hu
DOI: https://doi.org/10.1016/j.msea.2022.143532
2022-08-11
Abstract:In this paper, a series of Cu-3.2Ni-0.6Co-xSi-0.2Cr-0.15 Mg (x = 0.62, 0.75, 0.92 and 1.09) (wt.%) alloys were fabricated and subjected to multi-step thermo-mechanical treatment (TMT), and the microstructure and properties of the alloys were investigated in detailed. The results showed that the alloys achieved the combination of high strengths and high conductivity, i.e. yield strengths of 809–913 MPa, tensile strengths of 849–951 MPa, and electrical conductivity of 33.4–42.0 %IACS. The good properties were due to nanoscale δ-(Ni,Co)2Si and Cr3Si precipitates, high-density dislocations, and even deformation twins. More importantly, it is found that the Ni, Co and Cr solute atoms decreased but the Si solute atoms increased with the Si contents in the alloys according to the principle of conservation of mass. For deformation, this change aggravated dislocation annihilation, reduced twinning propensity, and thus weakened the work-hardening effect. For precipitation, this change promoted the coarsening of nanoscale precipitates and the depletion of solute atoms, and thus weakened the precipitation-strengthening effect but benefited the electrical conductivity.
materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering