A Low Temperature NO2 Sensor Based on SnSe2/SnO2 Heterojunction
Baoyu Huang,Xinyu Li,Xiaogan Li
DOI: https://doi.org/10.1149/ma2021-01561473mtgabs
2020-01-01
Abstract:Introduction Nitrogen dioxide (NO 2 ) is one of the main air pollutants which is harmful to human health. A Higher concentration of NO 2 may cause serious damage to respiratory system and even death. Moreover, the concentration of NO 2 in the exhaled breath can be regarded as a diagnostic marker of asthma. Therefore, it is necessary to develop a low-energy consumption gas sensor which can sensitive and accurate analysis of NO 2 in the atmosphere and exhaled breath. In this aspect, two dimensional (2D) layered nanostructured materials such as metal dichalcogenides (MX 2 , M=Mo, W, Sn etc..; X=S, Se, Te etc..) have received widespread attentions in NO 2 detection due to their high specific surface area and unique electrical properties[1]. For example, SnS 2 demonstrated excellent NO 2 sensing properties [2]. Moreover, as reported in literature [3], the formation of SnO 2 /SnS 2 heterostructure is beneficial to the further improvement of sensing performance. However, the gas sensing properties of SnSe are rarely reported. Therefore, the gas sensing properties of SnSe 2 and SnSe 2 /SnO 2 heterojunctions have investigated in this work. The SnSe 2 /SnO 2 heterojunctions displays much improved sensitivity and superior selectivity toward NO 2 at 120 °C. Experiment The SnSe 2 powder was purchased from Chengdu Alfa Metal Material Co. Ltd. After grinding for half an hour, the SnSe 2 powder was dispersed in an alcohol solution to obtain suspension by ultrasonic treatment. The paste was deposited onto the alumina substrates with Au interdigital electrodes. Then, the sensors were dried at 70 °C for 12 h. The SnSe 2 /SnO 2 heterojunction based sensor was obtained by in-situ oxidation SnSe 2 at 500 °C for 1 h in simulation air which is composed of 84.8 % dry nitrogen and 15.2 % dry oxygen. For comparison, the SnO 2 sensor was also prepared by in-situ oxidation SnSe 2 at 750 °C. Results and conclusions 1. Structure and Morphology Fig.1a shows the XRD patterns of SnSe 2 , SnO 2 and SnSe 2 /SnO 2 , respectively. For the SnSe 2 /SnO 2 sample, the diffraction peaks located at (001), (002), (003), (004), (005) lattice planes are assigned to the hexagonal SnSe 2 (JCPDS Card No. 89-2939) [4], and the other diffraction peaks are consistent with tetragonal SnO 2 (JCPDS No. 41-1445). No third phase was observed in the SnSe 2 /SnO 2 sample indicating the product with high purity. This is consistent with the HRTEM analysis. As shown in Fig. 1(b), the fringe spacing of 0.296 nm and 0.192 nm are corresponded to the d-spacing of (002) and (003) crystal planes of SnSe 2 , whereas the fringe spacing of 0.340 nm and 0.265 nm are assigned to the d-spacing of (110) and (101) crystal planes of SnO 2 . Additionally, the EDX mapping images and EDX spectrum of SnSe 2 /SnO 2 sample are shown in Fig.1c-d. It can be noticed that there only exist Sn, Se, and O elements in the composites material, and Sn (yellow), Se(red), and O (green) elements are uniformly distributed in the material, which confirming that the formation of SnO 2 nanocrystals on the surface of SnSe 2 and the oxidation of SnSe 2 to SnSe 2 /SnO 2 is partial. 2. Gas-Sensing Properties Fig. 2a shows the dynamic response and recovery curve of sensors to 8 ppm NO 2 at 120 °C. Compared to pristine SnSe 2 and SnO 2 based sensor, the SnSe 2 /SnO 2 based sensor exhibits the highest response value (5.6), which is approximately 10 times higher than that of SnSe 2 based sensor (0.54). In contrast, since SnO 2 didn’t work at the optimum temperature (usually at 200-400 °C), the redox reactions to induce a sensor response were almost inertia at 120 °C. The selectivity of the SnSe 2 /SnO 2 based sensor to several VOCs, including ethanol, ammonia, formaldehyde, acetone and methanol at 8 ppm in Fig. 2b. The response towards 8 ppm NO 2 is much higher compared to the other tested gases indicating a possible excellent selectivity towards NO 2 . The above results fully prove that the formation of SnSe 2 /SnO 2 heterojunctions can enhance the sensing performance of materials. References [1]. S. Cui, Z. Wen, X. Huang, J. Chang, J. Chen, Stabilizing MoS 2 Nanosheets through SnO 2 Nanocrystal Decoration for High-Performance Gas Sensing in Air, Small. 11 (2015) 2305–2313. doi: 10.1002/smll.201402923. [2]. J. Ou, W. Ge, B. Carey, T. Daeneke, A. Rotbart, W. Shan, Y. Wang, Z. Fu, A.F. Chrimes, W. Wlodarski, S.P. Russo, Y. Li, K. Kalantar-zadeh, Physisorption-Based Charge Transfer in Two-Dimensional SnS 2 for Selective and Reversible NO 2 Gas Sensing, ACS Nano. 9 (2015) 10313–10323. doi: 10.1021/acsnano.5b04343. [3]. D. Gu, X. G. Li, Y. Y. Zhao, J. Wang, Enhanced NO 2 Sensing of SnO 2 /SnS 2 Heterojunction Based Sensor, Sensors and Actuators B: Chemical. 244 (2017) 67–76. doi: 10.1016/j.snb.2016.12.125. [4] Y. Wang, L. Huang, B. Li, J. M. Shang, C. X. Xia, C. Fan, H.-X. Deng, Z. M. Wei, J. B. Li, Composition-Tunable 2D SnSe 2(1-x) S 2x Alloys towards Efficient Bandgap Engineering and High Performance (Opto)Electronics†, Journal of Materials Chemistry C. 5 (2017) 84-90. doi:10.1039/C6TC03751H. Figure 1